ARLEN™E430N
聚酰胺 6T
30% 玻璃纤维增强材料
Mitsui Chemicals, Inc.
产品说明：
ARLEN™ E430N by Mitsui Chemicals is a modified polyamide 6Treinforced with 30% glass fiber. Possesses high dimensionalstability, high melting point, high rigidity and minimum waterabsorption. Exhibits good chemical and heat resistance. Is suitablefor processing by injection molding. ARLEN™ E430N is recommendedfor electrical & electronic parts including connectors, jacks,switches and power supply terminals. Complies with UL 94 V-0 flamerating.
ARLEN™ E430N 物性表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 1.66 | g/cm³ | ASTM D792 |
| 收缩率 |
|
| ASTM D955 |
| 流动 | 0.30 | % | ASTM D955 |
| 横向流动 | 0.90 | % | ASTM D955 |
| 吸水率 (23°C, 24 hr, 65%r.h) | 1.9 | % | ASTM D570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 (M级) | 100 |
| ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 | 170 | MPa | ASTM D638 |
| 伸长率 (断裂) | 3.0 | % | ASTM D638 |
| 弯曲模量 | 11400 | MPa | ASTM D790 |
| 弯曲强度 | 250 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 | 80 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 (1.8 MPa, 未退火) | 305 | °C | ASTM D648 |
| 玻璃转化温度 | 95.0 | °C |
|
| 熔融温度 | 320 | °C |
|
| 线形热膨胀系数 |
|
| ASTM E831 |
| 流动 | 2.2E-5 | cm/cm/°C | ASTM E831 |
| 横向 | 7.3E-5 | cm/cm/°C | ASTM E831 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 体积电阻率 | 1.0E+15 | ohms·cm | ASTM D257 |
| 介电强度 | 24 | kV/mm | ASTM D149 |
| 介电常数 (1MHz) | 3.60 |
| ASTM D150 |
| 耗散因数 (1MHz) | 0.012 |
| ASTM D150 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|
| UL 阻燃等级 | V-0 |
| UL 94 |