--0.968g/cm³ASTMD792 --0.970g/cm³ISO 1183室外适用性f1
UL 746CDetergent Resistancef4
UL 2157Detergent Resistancef3
UL 749硬度额定值单位制测试方法肖氏硬度 (邵氏 A, 15 秒,23°C, 2.00 mm)78
ISO 868弹性体额定值单位制测试方法拉伸应力 - 横向流量 (100应变,23°C)3.60MPaASTM D412, ISO 37抗张强度 - 横向流量 (断裂, 23°C)8.80MPaASTM D412, ISO 37伸长率 -横向流量 (断裂, 23°C)490%ASTM D412, ISO37撕裂强度 - 横向流量
23°C 127.0kN/mASTMD624 23°C 227kN/mISO 34-1压缩变形
70°C, 22hr 328%ASTMD395B 125°C, 70hr 437%ASTMD395B 70°C, 22hr 528%ISO815 125°C, 70hr 637%ISO815老化额定值单位制测试方法空气中拉伸强度的变化率 (150°C, 168hr)-1.0%ASTM D573, ISO 188空气中极限伸长率的变化率 (150°C, 168 hr)-3.0%ASTM D573, ISO188空气中硬度计硬度的变化率 (支撐 A, 150°C, 168hr)7.0
ASTM D573, ISO 188拉伸强度的变化率
ASTM D471, ISO 1817 23°C, 168 hr, 在10％盐酸中13%ASTM D471, ISO1817 23°C, 168 hr,在15％氯化钠中0.0%ASTM D471, ISO1817 23°C, 168 hr,在2.5％洗涤剂中（汰渍）3.0%ASTM D471, ISO1817 23°C, 168 hr,在50%氢氧化钠中3.0%ASTM D471, ISO1817 23°C, 168 hr,在95％乙醇中-2.0%ASTM D471, ISO1817 23°C, 168 hr,在98％硫酸中-17%ASTM D471, ISO1817 23°C, 168 hr,在醋酸中-8.0%ASTM D471, ISO1817 23°C, 168 hr,在环己烷中31%ASTM D471, ISO1817 23°C, 168 hr,在甲乙酮中47%ASTM D471, ISO1817 23°C, 168 hr,在异丙醇中31%ASTM D471, ISO1817 23°C, 168 hr,在在三氯乙烯中54%ASTM D471, ISO1817 100°C, 168 hr,在IRM 903油中-30%ASTM D471, ISO1817 100°C, 168 hr,在去离子水中1.0%ASTM D471, ISO1817 125°C, 70 hr,在IRM 903油中-31%ASTM D471, ISO1817 125°C, 168 hr,在IRM 903油中-31%ASTM D471, ISO 1817极限伸长率的变化率
ASTM D471, ISO 1817 23°C, 168 hr, 在10％盐酸中9.0%ASTM D471, ISO1817 23°C, 168 hr,在15％氯化钠中-2.0%ASTM D471, ISO1817 23°C, 168 hr,在2.5％洗涤剂中（汰渍）2.0%ASTM D471, ISO1817 23°C, 168 hr,在50%氢氧化钠中2.0%ASTM D471, ISO1817 23°C, 168 hr,在95％乙醇中0.0%ASTM D471, ISO1817 23°C, 168 hr,在98％硫酸中-27%ASTM D471, ISO1817 23°C, 168 hr,在醋酸中-4.0%ASTM D471, ISO1817 23°C, 168 hr,在环己烷中20%ASTM D471, ISO1817 23°C, 168 hr,在甲乙酮中24%ASTM D471, ISO1817 23°C, 168 hr,在异丙醇中20%ASTM D471, ISO1817 23°C, 168 hr,在在三氯乙烯中22%ASTM D471, ISO1817 100°C, 168 hr,在IRM 903油中-49%ASTM D471, ISO1817 100°C, 168 hr,在去离子水中-7.0%ASTM D471, ISO1817 125°C, 70 hr,在IRM 903油中-47%ASTM D471, ISO1817 125°C, 168 hr,在IRM 903油中-58%ASTM D471, ISO 1817