POM深圳杜邦100具体内容
100P 物性表
性能额定值单位测试方法吸水量
ASTM D-570 (50%相对湿度)0.21%
(24小时浸渍)0.23%
(浸渍平衡点)0.90%
比重1.41
ASTM D-792自燃性HB
UL 94IZOD冲击试验 (无缺口23℃)>5300j/mASTM D-256破裂点拉伸变形量(100℃)>260%ASTM D-638洛氏硬度94M scaleASTM D-785挠曲系数(70℃)1580MPaASTM D-790线性热膨胀系数 (104-160℃)14.010-5m/m℃ASTMD-696破裂点拉伸变形量 (-55℃)40%ASTM D-638挠曲变形强度 (23℃)98MPaASTMD-790熔点175℃ASTM D-2133热畸变温度
ASTM D-648 (1.8MPa)136℃
(0.5MPa)172℃
挠曲系数 (122℃)685MPaASTM D-790抗剪强度 (23℃)66MPaASTM D-732IZOD冲击试验(23℃)135j/mASTM D-256拉伸强度 (70℃)45MPaASTM D-638压缩应力(23℃,10%变形)123MPaASTM D-695破裂点拉伸变形量 (23℃)65%ASTM D-638抗电弧(3.1mm)220secASTM D-495弹性系数 (23℃)3220MPaASTM D-638IZOD冲击试验(缺口-40℃)95j/mASTM D-256抗拉伸冲击强度 (长试片23℃)525kj/mASTMD-1822模收缩2.2-2.4%ASTM D-2133拉伸强度 (122℃)26MPaASTM D-638介电强度 (瞬间Shorttime(2.3mm))19.7kv/mmASTM D-149
POM深圳杜邦500P
500P 内容栏
性能额定值单位测试方法模收缩2.2-2.4%
比重1.41
ASTM D-792吸水量
ASTM D-570 (浸渍平衡点)0.80%
(50%相对湿度)0.20%
(24小时浸渍)0.26%
挠曲系数 (122℃)755MPaASTM D-790压缩应力 (23℃,10%变形)123MPaASTM D-695IZOD冲击试验(23℃)81j/mASTM D-256熔点175℃ASTM D-2133挠曲疲劳忍耐限度(50%RH,23℃,10周期)31MPaASTM D-671洛氏硬度94M scaleASTM D-785挠曲系数(100℃)1030%ASTM D-790破裂点拉伸变形量 (70℃)220%ASTM D-638挠曲系数(23℃)3090MPaASTM D-790抗电弧 (3.1mm)220secASTM D-495压缩应力(23℃,1%变形)35MPaASTM D-695破裂点拉伸变形量 (122℃)>260%ASTM D-638弹性系数(23℃)3360MPaASTM D-638容积电阻率 (23℃,0.2%含水量)1×10Ω.cmASTM D-257洛氏硬度120RscaleASTM D-785破裂点拉伸变形量 (23℃)35%ASTM D-638IZOD冲击试验(无缺口23℃)2160j/mASTM D-256热畸变温度 (1.8MPa)136MPaASTM D-648线性热膨胀系数(-40-29℃)13.710-5m/m℃ASTM D-696挠曲变形强度 (23℃)97MPaASTM D-790拉伸强度(23℃)69MPaASTM D-638IZOD冲击试验 (缺口-40℃)66j/mASTM D-256抗剪强度(23℃)66MPaASTM D-732