PA66 德国巴斯夫 A3X2G5 玻纤25% 阻燃V0 红磷无卤
产品参数
Ultramid? A3X2G5
聚酰胺66
25% 玻璃纤维增强材料
BASF Corporation
产品说明:
Ultramid A3X2G5 is a 25% glass fiber reinforced injection moldingPA66 grade with improved flame retardance and enhanced long-termperformance. Flame retardant based on red phosphorus; outstandingmechanical and electrical properties.
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
比重 | ||||
-- | 1.34 | -- | ASTM D792 | |
-- | g/cm3 | ISO 1183 | ||
溶化体积流率（MVR）(275°C/5.0 kg) | 2.44 | in3/10min | ISO 1133 | |
收缩率 - 流动(0.125 in) | 5.0E-3 | in/in | ||
吸水率 | ||||
饱和 | 6.0 | % | ASTM D570 | |
饱和, 73°F | ISO 62 | |||
平衡, 50% RH | 1.4 | ASTM D570 | ||
平衡, 73°F, 50% RH | ISO 62 |
| 机械性能 | 干燥 | |||
拉伸模量(73°F) | 1.23E+6 | 870000 | psi | ISO 527-2 |
抗张强度 | ||||
断裂, 73°F | 20000 | ASTM D638 | ||
断裂, -40°F | 28400 | ISO 527-2 | ||
断裂, 73°F | 20300 | 14500 | ISO 527-2 | |
伸长率 | 3.0 | ASTM D638 | ||
断裂, 73°F | 4.5 | ISO 527-2 | ||
弯曲模量(73°F) | 1.03E+6 | ASTM D790 | ||
| 冲击性能 | 干燥 | |||
简支梁缺口冲击强度 | ISO 179 | |||
-22°F | 4.8 | ft·lb/in2 | ||
73°F | 6.2 | 8.1 | ||
简支梁无缺口冲击强度 | 29 | 31 | 33 |