| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 103 | 103 | ASTM D785 |
| 抗张强度(屈服) | 44.1 MPa @Thickness 3.20 mm | 6400 psi @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 20 % @Thickness 3.20 mm | 20 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 屈服伸长率 | >= 5.0 % @Thickness 3.20 mm | >= 5.0 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| 拉伸模量 | 2.16 GPa @Thickness 3.20 mm | 313 ksi @Thickness 0.126 in | 1 mm/min; ASTM D638 |
| 弯曲强度 | 68.6 MPa @Thickness 6.40 mm | 9960 psi @Thickness 0.252 in | 15 mm/min; ASTM D790 |
| 弯曲模量 | 2.35 GPa @Thickness 6.40 mm | 341 ksi @Thickness 0.252 in | 15 mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.77 J/cm @Thickness 6.40 mm, Temperature 23.0 °C | 3.31 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F | ASTM D256 |
| 2.06 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 3.86 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | |
| Izod Impact, Unnotched | 0.588 J/cm @Thickness 6.40 mm, Temperature -30.0 °C | 1.10 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F | ASTM D256 |
| 0.588 J/cm @Thickness 3.20 mm, Temperature -30.0 °C | 1.10 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F | ASTM D256 |
<table class="table property_table" font-size:14px;"=""style="border-spacing: 0px; width: 722px; font-family: 宋体;font-size: 12px; white-space: normal; background-color: rgb(255,255, 255); color: rgb(51, 51, 51);">
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|