TPE THERMOLAST K TC2TPN
| Product Description | |
The GP/AP Series is your material solution for technicalapplications with excellent adhesion to PP. The compounds areavailable in natural and black colors.Typicalapplications
Material advantages
| |
| General | |
Material Status |
|
Availability |
|
Features | Good AdhesionGood ColorabilityGood FlowGood WeatherResistance |
Uses | HandlesSoft Touch ApplicationsSwitches |
Appearance |
|
Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
Density | g/cm3 | ISO 1183 | |
| Elastomers | Nominal Value | Unit | Test Method |
Tensile Stress2(Yield) | psi | ISO 37 | |
Tensile Elongation2(Break) | % | ISO 37 | |
Tear Strength3 | lbf/in | ISO 34-1 | |
Compression Set4 | ISO 815 | ||
73°F, 72 hr | % | ||
158°F, 24 hr | % | ||
212°F, 24 hr | % | ||
| Hardness | Nominal Value | Unit | Test Method |
Shore Hardness(Shore A) | ISO 7619 |
TPE THERMOLAST K TC2TPN
TPE是一种具有橡胶的高弹性，高强度，高回弹性，又具有可注塑加工的特征，具有环保无毒安全，硬度范围广，有优良的着色性，触感柔软，耐候性，抗疲劳性和耐温性，加工性能优越，无须硫化，可以循环使用降低成本，既可以二次注塑成型，与PP、PE、PC、PS、ABS等基体材料包覆粘合，也可以单独成型。
优点：
一、易于回收利用，降低成本。生产过程中产生的废料和*终出现的废品，可以直接返回再利用；用过的TPE旧品可以简单再生之后回收利用，减少环境污染，扩大再生资源来源。
二、节能：热塑性弹性体大多不需要硫化或硫化时间很短，可以有效节约能源。
三、可用一般的热塑性塑料成型机加工，不需要特殊的加工设备。
四、生产效率大幅提高。可直接用橡胶注塑机硫化，时间由原来的20min左右，缩短到1min以内；由于需要的硫化时间很短，因此已可用挤出机直接硫化，生产效率大幅提高。
特点:
1.可用一般的热塑性塑料成型机加工，不需要特殊的加工设备。
2.生产效率大幅提高。可直接用橡胶注塑机硫化，时间由原来的20min左右，缩短到1min以内；由于需要的硫化时间很短，因此已可用挤出机直接硫化，生产效率大幅提高。
3.易于回收利用，降低成本。生产过程中产生的废料（逸出毛边、挤出废胶）和*终出现的废品，可以直接返回再利用；用过的TPE旧品可以简单再生之后回收利用，减少环境污染，扩大再生资源来源。
4.节能。热塑性弹性体大多不需要硫化或硫化时间很短，可以有效节约能源。以高压软管生产能耗为例：橡胶为188MJ/kg，TPE为144MJ/kg，可节能达25%以上。
5. 应用领域更广。由于TPE兼具橡胶和塑料的优点，为橡胶工业开辟了新的应用领域。
6.可用于塑料的增强、增韧改性。自补强性大，配方简化，配合剂对聚合物的影响制约小，质量性能更易掌握。但TPE的耐热性不如橡胶，随着温度上升而物性下降幅度较大，因而适用范围受到限制。同时，压缩变形、弹性回复、耐久性等同橡胶相比较差，价格上也往往高于同类橡胶。尽管如此，TPE的优点仍十分突出，各种新型的TPE产品也不断开发出来。作为一种节能环保的橡胶新型原料，发展前景十分看好。
TPE THERMOLAST KTC2TPN我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！