| Testitem 测试名称： | |
| TestFor Flammability of Plastic Materials for Parts in Devices andAppliances | |
| 设备和器具部件材料的可燃性能试验 | |
| Testinfo 测试内容： | |
| Test Items | Relevant Standards |
| 水平燃烧(自撑料) | UL 94:1997, ASTMD635 |
| UL94 HB | IEC 60695-11-10 |
| conditioning | 23 ±2°C and 50±5 percentrelative humidity for a minimum of 48 hours |
| 垂直燃烧(自撑料) | ASTM D3801-00/IEC60695-11-10 |
| UL94V0,V1,V2 | |
| conditioning | 23 ±2°C and 50±5 percentrelative humidity for a minimum of 48 hours and preconditioned inan air-circulating oven for 168 hours at 70±1°C and then cooled inthe desiccator for at least 4 hours at room temperature, prior totesting. |
| 垂直燃烧(自撑料) | ISO 1035 |
| UL94 5VA,5VB | ASTM D5048 |
| conditioning | 23 ±2°C and 50±5 percentrelative humidity for a minimum of 48 hours and preconditioned inan air-circulating oven for 168 hours at 70±1°C and then cooled inthe desiccator for at least 4 hours at room temperature, prior totesting. |
| 水平燃烧(泡沫材料) | ASTM D4986/ISO 3852 |
| UL94 HBF, HF-1,HF-2 | IEC 60695-11-10 |
| conditioning | 23 ±2°C and 50±5 percentrelative humidity for a minimum of 48 hours and preconditioned inan air-circulating oven for 168 hours at 70±1°C and then cooled inthe desiccator for at least 4 hours at room temperature, prior totesting. |
| 垂直燃烧(软质塑料) | ISO 9773 |
| UL94 VTM0, VTM-1,VTM-2 | ASTM D4804 |
| conditioning | 23 ±2°C and 50±5 percentrelative humidity for a minimum of 48 hours and preconditioned inan air-circulating oven for 168 hours at 70±1°C and then cooled inthe desiccator for at least 4 hours at room temperature, prior totesting. |
| Sample Required and TurnaroundTime, 所需样品及时间 | ||
| TestItems | TAT (WorkingDays) | |
| HB | 7 | |
| 12 pieces with the size of 125±5 mm long by 13.0 ±0.5 mm wide, and provided in the minimumthickness and 3.0 (-0.0 +0.2) mm thick. The 3.0 mm thick specimensare not necessary if the minimum thickness is greater than 3.0 mm,or the maximum thickness is less than 3.0 mm. The maximum thicknessis not to exceed 13 mm. The maximum width is not to exceed 13.5 mm,the edges are to be smooth, and the radius on the corners is not toexceed 1.3 mm. | ||
| 12 pieces with the size of (125± 5) × (13 ± 0,2) mm X thickness(需要提供测试的Zui小厚度样品和3毫米厚度样品,若样品Zui小厚度大于3mm,或者Zui大厚度小于3MM,则可以不用提供3mm样品;样品Zui大厚度不超过13mm,Zui大宽度不超过13.5mm,) | ||
| V0, V1, V2 | 14 | |
| 17 pieces with the size of 125±5 mm long by 13.0 ±0.5 mm wide, and provided in the minimum andmaximum thicknesses. The maximum thickness is not to exceed 13 mm.Specimens in intermediate thicknesses are also to be provided andshall be tested if the results obtained on the minimum or maximumthickness indicate inconsistent test results. Intermediatethicknesses are not to exceed increments of 3.2 mm. Also, the edgesare to be smooth, and the radius on the corners is not to exceed1.3 mm. | ||
| 17 pieces with the size of (125± 5) × (13 ± 0,2) mmX thickness(需要提供测试的Zui小厚度样品和Zui大样品厚度；样品Zui大厚度不超过13mm，如果Zui小厚度样品和Zui大厚度样品得出的结果不一致，则还需要提供中间尺寸样品，中间尺寸厚度跨度不超3.2mm) | ||
| 5VA, 5VB | 14 | |
| 32 pieces with (125 ± 5) × (13±0.5) mm X minimum thickness AND 10 pieces 150 ± 5 × 150± 5 mmX minimum thickness | ||
| 32 pieces with (125 ± 5) × (13±0.5) mm X Zui小厚度 和 10 pieces 150 ± 5 × 150± 5 mmXZui小厚度 (Zui大厚度不超过13mm) | ||
| HBF, HF-1, HF-2 | 14 | |
| 17 pieces 150 ±5 mm long by 50±1 mm wide, in the minimum and maximum thicknesses covering thethickness range to be considered. Specimens tested by this methodare limited to a maximum thickness of 13 mm. Specimens inintermediate thicknesses are also to be provided and shall betested if the results obtained on the minimum and/or maximumthickness indicate inconsistent test results. Intermediatethicknesses are not to exceed increments of 6 mm. The maximum widthis not to exceed 50 mm. The edges are to be smooth and the radiuson the corners is not to exceed 2 mm | ||
| 17 pieces (150± 5) X (50± 1) mmX thickness (Zui小厚度和Zui大厚度都要提供, 当Zui大厚度和Zui小厚度的测试结果不一致，则中间的厚度也要提供，间隔不要超过6mm，试样宽度不要超过50mm) | ||
| VTM0, VTM-1, VTM-2 | 14 | |
| 17 pieces, 200 ±5 mm in lengthby 50 ±1 mm in width, in the minimum and maximum thicknesses thatare to be tested covering the thickness range under consideration.Specimens in intermediate thicknesses are also to be provided andshall be tested. if the results obtained on the minimum and/ormaximum thicknesses indicated inconsistent test results | ||
| 17 pieces (200± 5) X (50± 1)mmX thickness (Zui小厚度和Zui大厚度都要提供，这样可以认为测试结果对整个厚度系列有效，但当Zui小厚度和Zui大厚度的测试结果不一致时，中间的厚度也要提供) | ||
Others其他信息:
1.UL94垂直燃烧，要求前处理70度168小时, 所以不能申请加急服务
2. Sample Report报告样本：