Test item 测试名称：
Test For Flammability of Plastic Materials for Parts in Devices andAppliances
设备和器具部件材料的可燃性能试验
Testinfo 测试内容： | |
| Test Items | RelevantStandards |
| 水平燃烧(自撑料) | UL 94:1997, ASTMD635 |
| UL94 HB | IEC 60695-11-10 |
| conditioning | 23 ±2°C and 50±5 percentrelative humidity for a minimum of 48 hours |
| 垂直燃烧(自撑料) | ASTM D3801-00/IEC60695-11-10 |
| UL94 V0,V1,V2 | |
| conditioning | 23 ±2°C and 50±5 percentrelative humidity for a minimum of 48 hours and preconditioned inan air-circulating oven for 168 hours at 70±1°C and then cooled inthe desiccator for at least 4 hours at room temperature, prior totesting. |
| 垂直燃烧(自撑料) | ISO1035 |
| UL94 5VA,5VB | ASTMD5048 |
| conditioning | 23 ±2°C and50±5 percent relative humidity for a minimum of 48 hours andpreconditioned in an air-circulating oven for 168 hours at 70±1°Cand then cooled in the desiccator for at least 4 hours at roomtemperature, prior to testing. |
| 水平燃烧(泡沫材料) | ASTMD4986/ISO 3852 |
| UL94 HBF, HF-1,HF-2 | IEC60695-11-10 |
| conditioning | 23 ±2°C and50±5 percent relative humidity for a minimum of 48 hours andpreconditioned in an air-circulating oven for 168 hours at 70±1°Cand then cooled in the desiccator for at least 4 hours at roomtemperature, prior to testing. |
| 垂直燃烧(软质塑料) | ISO9773 |
| UL94 VTM0, VTM-1,VTM-2 | ASTMD4804 |
| conditioning | 23 ±2°C and50±5 percent relative humidity for a minimum of 48 hours andpreconditioned in an air-circulating oven for 168 hours at 70±1°Cand then cooled in the desiccator for at least 4 hours at roomtemperature, prior to testing. |
| Sample Required and Turnaround Time,所需样品及时间 | ||
| Test Items | TAT (Working Days) | |
| HB | 7 | |
| 12 pieces with the size of 125 ±5 mm long by13.0 ±0.5 mm wide, and provided in the minimum thickness and 3.0(-0.0 +0.2) mm thick. The 3.0 mm thick specimens are not necessaryif the minimum thickness is greater than 3.0 mm, or the maximumthickness is less than 3.0 mm. The maximum thickness is not toexceed 13 mm. The maximum width is not to exceed 13.5 mm, the edgesare to be smooth, and the radius on the corners is not to exceed1.3 mm. | ||
| 12 pieces with the size of (125 ± 5) × (13 ±0,2) mm Xthickness(需要提供测试的Zui小厚度样品和3毫米厚度样品,若样品Zui小厚度大于3mm,或者Zui大厚度小于3MM,则可以不用提供3mm样品;样品Zui大厚度不超过13mm,Zui大宽度不超过13.5mm,) | ||
| V0, V1, V2 | 14 | |
| 17 pieces with the size of 125 ±5 mm long by13.0 ±0.5 mm wide, and provided in the minimum and maximumthicknesses. The maximum thickness is not to exceed 13 mm.Specimens in intermediate thicknesses are also to be provided andshall be tested if the results obtained on the minimum or maximumthickness indicate inconsistent test results. Intermediatethicknesses are not to exceed increments of 3.2 mm. Also, the edgesare to be smooth, and the radius on the corners is not to exceed1.3 mm. | ||
| 17 pieces with the size of (125 ± 5) × (13 ±0,2) mmXthickness(需要提供测试的Zui小厚度样品和Zui大样品厚度；样品Zui大厚度不超过13mm，如果Zui小厚度样品和Zui大厚度样品得出的结果不一致，则还需要提供中间尺寸样品，中间尺寸厚度跨度不超3.2mm) | ||
| 5VA, 5VB | 14 | |
| 32 pieces with (125 ± 5) × (13± 0.5) mm Xminimum thickness AND 10 pieces 150 ± 5 × 150± 5 mm X minimumthickness | ||
| 32 pieces with (125 ± 5) × (13± 0.5) mm XZui小厚度和 10 pieces 150 ± 5 × 150± 5 mm XZui小厚度 (Zui大厚度不超过13mm) | ||
| HBF, HF-1,HF-2 | 14 | |
| 17 pieces 150 ±5 mm long by 50 ±1 mm wide, inthe minimum and maximum thicknesses covering the thickness range tobe considered. Specimens tested by this method are limited to amaximum thickness of 13 mm. Specimens in intermediate thicknessesare also to be provided and shall be tested if the results obtainedon the minimum and/or maximum thickness indicate inconsistent testresults. Intermediate thicknesses are not to exceed increments of 6mm. The maximum width is not to exceed 50 mm. The edges are to besmooth and the radius on the corners is not to exceed 2mm | ||
| 17 pieces (150± 5) X (50± 1) mm X thickness(Zui小厚度和Zui大厚度都要提供,当Zui大厚度和Zui小厚度的测试结果不一致，则中间的厚度也要提供，间隔不要超过6mm，试样宽度不要超过50mm) | ||
| VTM0,VTM-1,VTM-2 | 14 | |
| 17 pieces, 200 ±5 mm in length by 50 ±1 mm inwidth, in the minimum and maximum thicknesses that are to be testedcovering the thickness range under consideration. Specimens inintermediate thicknesses are also to be provided and shall betested. if the results obtained on the minimum and/or maximumthicknesses indicated inconsistent test results | ||
| 17 pieces (200± 5) X (50± 1)mm X thickness(Zui小厚度和Zui大厚度都要提供，这样可以认为测试结果对整个厚度系列有效，但当Zui小厚度和Zui大厚度的测试结果不一致时，中间的厚度也要提供) | ||
Others 其他信息:
1.UL94垂直燃烧，要求前处理70度168小时, 所以不能申请加急服务
2. SampleReport 报告样本：