高透明 PC 基础创新塑料DMX9455-BK1D046 阻燃 注塑级防弹胶
DMX9455
聚碳酸酯#防弹胶|PC
沙伯基础（原GE）
加工方式:注射成型
填充物:透明,阻燃 注塑
外观:清晰/透明
物性信息：
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 比重 | |||
| 1.20 | g/cm | ASTM D792 | |
| 1.17 | g/cm | ISO 1183,ASTM D792 | |
| 特定体积 | 0.850 | cm/g | ASTM D792 |
| 熔流率 (300℃/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| 溶化体积流率(MVR) (300℃/1.2 kg) | 13.5 | cm/10min | ISO 1133 |
| 收缩率 (流动: 3.20 mm) | 0.50 到 0.80 | % | Internal Method |
| 吸水率 | |||
| ( 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| ( 24 hr, ) | 0.080 | % | ASTM D570 |
| ( 饱和, 23℃ ) | 0.27 | % | ISO 62 |
| ( 平衡, 23℃ ) | 0.28 | % | ASTM D570 |
| (平衡, 50% RH) | 0.13 | % | ASTM D570 |
| ( 平衡, 23℃, 50% RH ) | 0.13 | % | ISO 62 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 | |||
| (L 计秤) | 108 | ASTM D785 | |
| (M 计秤) | 93 | ASTM D785 | |
| 球压硬度 (H 358/30) | 128 | MPa | ISO 2039-1 |
| Erichson Scratch Depth - 6N | 14.0 | µm | Internal Method |
| Pencil Hardness | H | ASTM D3363 | |
| 拉伸模量 | |||
| 2900 | MPa | ASTM D638 | |
| 2450 | MPa | ISO 527-2/1 | |
| 抗张强度 | |||
| (屈服) | 80.0 | MPa | ASTM D638 |
| (屈服) | 80.0 | MPa | ISO 527-2/50 |
| (断裂) | 65.0 | MPa | ASTM D638 |
| (断裂) | 60.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| (屈服) | 7.0 | % | ASTM D638 |
| (屈服) | 7.0 | % | ISO 527-2/50 |
| (断裂) | 70 | % | ASTM D638 |
| (断裂) | 40 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| (50.0 mm 跨距) | 2600 | MPa | ASTM D790 |
| 2450 | MPa | ISO 178 | |
| 弯曲强度 | |||
| 108 | MPa | ISO 178 | |
| (屈服, 50.0 mm 跨距) | 120 | MPa | ASTM D790 |
| 抗泰伯磨耗 | |||
| (1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 |
| (1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | Internal Method |
| 简支梁缺口冲击强度 | |||
| ( -30℃ ) | 3.0 | kJ/m | ISO 179/1eA |
| (23℃) | 3.0 | kJ/m | |
| ( -30℃ ) | 47 | kJ/m | ISO 179/1eU |
| (23℃) | 无断裂 | ||
| 悬壁梁缺口冲击强度 | |||
| (-30℃) | 30 | J/m | ASTM D256 |
| (23℃) | 30 | J/m | ASTM D256 |
| (-30℃) | 4.0 | kJ/m | ISO 180/1A |
| (23℃) | 5.0 | kJ/m | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| (23℃) | 无断裂 | ASTM D4812, ISO 180/1U | |
| (-30℃) | 45 | kJ/m | ISO 180/1U |
| 装有测量仪表的落镖冲击 (23℃, Total Energy) | 30.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热变形温度 | |||
| ( 0.45 MPa, 未退火, 3.20 mm ) | 133 | ℃ | ASTM D648 |
| ( 0.45 MPa, 未退火, 64.0 mm 跨距 ) | 131 | ℃ | ISO 75-2/Bf |
| (1.8 MPa, 未退火, 3.20 mm) | 119 | ℃ | ASTM D648 |
| (1.8 MPa, 未退火, 64.0 mm 跨距) | 118 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| 139 | ℃ | ASTM D1525 | |
| 138 | ℃ | ISO 306/B50 | |
| 140 | ℃ | ISO 306/B120 | |
| Ball Pressure Test | |||
| (125℃) | Pass | IEC 60695-10-2 | |
| (140℃) | Pass | ||
| 线形膨胀系数 | |||
| ( 流动: -40 到 40℃ ) | 0.000030 | cm/cm/℃ | ASTM E831 |
| ( 流动: 23 到 80℃ ) | 0.000030 | cm/cm/℃ | ISO 11359-2 |
| ( 流动:-40 到 40℃ ) | 0.000070 | cm/cm/℃ | ASTM E831 |
| ( 流动: 23 到 80℃ ) | 0.000070 | cm/cm/℃ | ISO 11359-2 |
| 比热 | 1400 | J/kg/℃ | ASTM C351 |
| 导热系数 | 0.20 | W/m/K | ASTM C177, ISO 8302 |