供应 美国Ascend R525H 首诺PA66 玻纤增强 抗蠕变 高冲击

Physical Properties物理性质

Metric公制数据

English英制数据

Comments测试方法

Specific Gravity比重

1.32g/cc

1.32g/cc

ISO 1183

Water Absorption吸水率

0.85 %@Time 86400 sec

0.85 %@Time 24.0 hour

ISO 62

Moisture Absorption at Equilibrium吸湿平衡

2.0 %

2.0 %

50% RH; ISO 62

Linear Mold Shrinkage线性收缩率

0.0040cm/cm@Thickness 2.00 mm

0.0040in/in@Thickness 0.0787 in

ISO 294-4

Linear Mold Shrinkage, Transverse线性收缩率/横向

0.0090cm/cm@Thickness 2.00 mm

0.0090in/in@Thickness 0.0787 in

ISO 294-4

Mechanical Properties力学性能

Metric公制数据

English英制数据

Comments测试方法

Tensile Strength at Break断裂拉伸强度

174MPa

25200psi

ISO 527

Elongation at Break断裂伸长率

3.5 %

3.5 %

ISO 527

Tensile Modulus拉伸模量

7.50GPa

1090ksi

ISO 527

Flexural Strength

250MPa

36300psi

ISO 178

Flexural Modulus弯曲弹性模量

7.70GPa

1120ksi

ISO 178

Poissons Ratio泊松比

0.40

0.40

ISO 527

Shear Modulus剪切模量

2.68GPa

389ksi

Calculated

Izod Impact, Notched悬臂梁缺口冲击强度(ISO)

7.10kJ/m2

3.38ft-lb/in2

ISO 180

Charpy Impact Unnotched夏比缺口试样冲击

3.90J/cm2@Temperature -30.0 °C

18.6ft-lb/in2@Temperature -22.0 °F

ISO 179

4.20J/cm2@Temperature 23.0 °C

20.0ft-lb/in2@Temperature 73.4 °F

ISO 179

Charpy ImPAct, Notched夏比缺口冲击

0.980J/cm2@Temperature -30.0 °C

4.66ft-lb/in2@Temperature -22.0 °F

ISO 179

1.09J/cm2@Temperature 23.0 °C

5.19ft-lb/in2@Temperature 73.4 °F

ISO 179

Electrical Properties电性能

Metric公制数据

English英制数据

Comments测试方法

Volume ResiSTivity体积电阻率

3.00e 15ohm-cm@Thickness 3.00 mm

3.00e 15ohm-cm@Thickness 0.118 in

IEC 60093

Dielectric Strength介电强度

16.0kV/mm@Thickness 3.00 mm

406kV/in@Thickness 0.118 in

IEC 60243

Comparative Tracking Index跟踪指数

400-599V@Thickness 3.00 mm

400-599V@Thickness 0.118 in

IEC 60112

Thermal Properties热性能

Metric公制数据

English英制数据

Comments测试方法

CTE, linear线性热膨胀系数

3.50μm/m-°C@Thickness 2.00 mm,Temperature 23.0 - 55.0°C

1.94μin/in-°F@Thickness 0.0787 in,Temperature 73.4 - 131°F

ISO 11359

CTE, linear, Transverse to Flow线性热膨胀系数/横向

11.0μm/m-°C@Thickness 2.00 mm,Temperature 23.0 - 55.0°C

6.11μin/in-°F@Thickness 0.0787 in,Temperature 73.4 - 131°F

ISO 11359

Melting Point熔点

260°C

500°F

ISO 3146

Deflection Temperature at热变形温度0.46 MPa (66psi)

258°C

496°F

ISO 75

Deflection Temperature at热变形温度1.8 MPa (264psi)

250°C

482°F

ISO 75

Vicat Softening Point维卡软化点

251°C@Load 5.10 kg

484°F@Load 11.2 lb

ISO 306

Processing Properties加工性能

Metric公制数据

English英制数据

Comments测试方法

Processing Temperature加工温度

280-310°C

536-590°F

Melt Temperature熔体温度

285-305°C

545-581°F

Mold Temperature模具温度

65.0-95.0°C

149-203°F

Injection Pressure注射压力

55.0-140MPa

7980-20300psi

Hold Pressure保持压力

55.0-140MPa

7980-20300psi

Back Pressure背压

0.200-1.00MPa

29.0-145psi

Clamp Pressure压钳

29.43-68.67MPa

4268-9960psi

Cushion缓冲

0.300-0.640cm

0.118-0.252in

Screw Speed螺杆速度

60-120rpm

60-120rpm