30% 碳石墨PTFE增强 150FC30 英国威格斯 peek 低摩擦 耐化学高强度
VICTREX®PEEK 150FC30
Polyetheretherketone
Victrex plc
30% 碳石墨PTFE
产品说明：
High performance thermoplastic material, 30% reinforced withcarbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semicrystalline, granules for injection moulding, easy flow, FDA foodcontact compliant, colour black.
Tribological applications with thin cross sections or long flowlengths for high strength. Excellent wear resistance, very lowcoefficient of friction, low coefficient of thermal expansion.Chemically resistant to aggressive environments.
物性信息：
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 特性 |
|
| 机构评级 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 1 | 1.45 | g/cm³ | ISO 1183 |
| Spiral Flow | 13.0 | cm | 内部方法 |
| 收缩率 2 | ISO 294-4 | ||
| 流动方向 :180°C | 0.20 | % | ISO 294-4 |
| 垂直流动方向 : 180°C, 3.00mm | 0.70 | % | ISO 294-4 |
| 吸水率 | ISO 62 | ||
| 23°C, 24 hr, 3.20mm | 0.040 | % | ISO 62 |
| 平衡, 23°C, 3.20 mm,50% RH | 0.30 | % | ISO 62 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D, 23°C) | 83 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 (23°C) | 12500 | MPa | ISO 527-2 |
| 拉伸应力 | ISO 527-2 | ||
| 断裂, 23°C | 150 | MPa | ISO 527-2 |
| 断裂, 125°C | 100 | MPa | ISO 527-2 |
| 断裂, 175°C | 65.0 | MPa | ISO 527-2 |
| 断裂, 225°C | 50.0 | MPa | ISO 527-2 |
| 断裂, 275°C | 35.0 | MPa | ISO 527-2 |
| 拉伸应变 (断裂, 23°C) | 2.0 | % | ISO 527-2 |
| 弯曲模量 (23°C) | 11500 | MPa | ISO 178 |
| 弯曲应力 | ISO 178 | ||
| 23°C | 220 | MPa | ISO 178 |
| 125°C | 160 | MPa | ISO 178 |
| 175°C | 80.0 | MPa | ISO 178 |
| 275°C | 45.0 | MPa | ISO 178 |
| 压缩应力 | ISO 604 | ||
| 23°C | 170 | MPa | ISO 604 |
| 120°C | 110 | MPa | ISO 604 |