高流动 KT-820 GF15 美国索尔维 PEEK 加纤15% 连接器 泵件工业应用
KetaSpire®KT-820 GF15
Polyetheretherketone
Solvay Specialty Polymers
15% 玻璃纤维增强材料
产品说明:
KetaSpire® KT-820 GF15 is a low flow, 15% glass-fiber reinforcedgrade of polyetheretherketone (PEEK). This resin offers higherstrength and stiffness properties relative to unreinforcedKetaSpire® PEEK resin. The glass fiber content is optimized toprovide a balance of strength and stiffness with toughness-relatedproperties, such as impact resistance and elongation at break. Thelow fiberglass loading gives the resin improved surface aestheticsand reduced anisotropy over comparable 30% glass reinforcedformulations.
KetaSpire® PEEK is produced to the highest industry standards andis characterized by a distinct combination of properties, whichinclude excellent wear resistance, best-in-class fatigueresistance, ease of melt processing, high purity and excellentchemical resistance to organics, acids and bases.
These properties make it well-suited for applications in oil & gas,healthcare, transportation, electronics, chemical processing andother industrial uses.
Natural: KT-820 GF15 NT
物性信息:
基本信息 | |
---|---|
填料/增强材料 |
|
特性 |
|
用途 |
|
RoHS 合规性 |
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
比重 | 1.40 | g/cm³ | ASTM D792 |
灰份含量 | 15 | % | ISO 3451-1 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
弹性模量 | 6.10 | GPa | ASTM D638 |
拉伸模量 | 6200 | MPa | ASTM D638 |
拉伸应力 (断裂) | 124 | MPa | ASTM D638 |
拉伸应变 1(断裂) | 5.0 | % | ASTM D638 |
弯曲应力 | 205 | MPa | ASTM D638 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 | 9.5 | kJ/m² | ISO 179 |
简支梁无缺口冲击强度 | 85 | kJ/m² | ISO 179 |
悬壁梁缺口冲击强度 | 9.0 | kJ/m² | ISO 180 |
无缺口伊佐德冲击强度 | 74 | kJ/m² | ISO 180 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
热变形温度 (1.8 MPa, 未退火) | 218 | °C | ISO 75-2/A |