耐化学 Evonik 2000G 德国赢创德固赛 PEEK 中粘度 自熄 半结晶
VESTAKEEP®2000G
Polyetheretherketone
Evonik Industries AG
产品说明:
Medium-viscosity, unreinforced polyether ether ketone
VESTAKEEP 2000G is a medium-viscosity, unreinforced polyether etherketone for injection molding.
The semi-crystalline polymer features superior thermal and chemicalresistance. Parts made from VESTAKEEP 2000G areself-extinguishing.
VESTAKEEP 2000G can be processed by common injection moldingmachines for thermoplastics.
We recommend a melt temperature between 360°C and 380°C during theinjection molding process. The mold temperature should be within arange of 160°C to 200°C, preferably 180°C.
物性信息:
基本信息 | |
---|---|
黄卡编号 |
|
特性 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.30 | g/cm³ | ISO 1183 |
溶化体积流率(MVR) (380°C/5.0 kg) | 70.0 | cm³/10min | ISO 1133 |
收缩率 1 | ISO 294-4 | ||
垂直流动方向 : 80°C, 2.00mm | 1.1 | % | ISO 294-4 |
流动方向 : 80°C, 2.00mm | 1.1 | % | ISO 294-4 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 3700 | MPa | ISO 527-2 |
拉伸应力 (屈服) | 100 | MPa | ISO 527-2 |
拉伸应变 | ISO 527-2 | ||
屈服 | 5.0 | % | ISO 527-2 |
断裂 | 30 | % | ISO 527-2 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 | ISO 179/1eA | ||
-30°C,完全断裂 | 6.0 | kJ/m² | ISO 179/1eA |
23°C,完全断裂 | 6.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 (23°C) | 无断裂 | ISO 179/1eU |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
维卡软化温度 | |||
-- | 335 | °C | ISO 306/A |
-- | 310 | °C | ISO 306/B |
熔融温度 2 | 340 | °C | ISO 11357-3 |
线形热膨胀系数 - 流动 (23 到 55°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
电气性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
表面电阻率 | 1.0E+14 | ohms | IEC 60093 |
体积电阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
介电强度 3 | 16 | kV/mm | IEC 60243-1 |
相对电容率 | IEC 60250 | ||
50 Hz | 2.80 | IEC 60250 | |
1 MHz | 2.80 | IEC 60250 | |
漏电起痕指数 | IEC 60112 | ||
解决方案A 4 | 175 | V | IEC 60112 |
解决方案 A | 200 | V | IEC 60112 |