高温尼龙 PA9T 日本可乐丽 G1300H 玻纤增强30% 无卤素 电气元件
Genestar™G1300H
Polyamide 9T
Kuraray Co., Ltd.
30% 玻璃纤维增强材料
产品说明：
The G1300H and G1350H are suitable for use in a wide range ofelectrical and electronics components as UL94 HB flammabilityrating, while the G1302 grade delivers low friction. HB grades donot contain halogen-containing flame-retardants. The GW1458HFoffers low warpage and high flow-ability.
*'Halogen free' follows the standards that Br is less than 900ppm,Cl is less than 900ppm, and total of halogen amount (Br and Cl) isless than 1500ppm.
物性信息：
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.37 | g/cm³ | |
| 熔流率（熔体流动速率） (320°C/2.16 kg) | 45 | g/10 min | ASTM D1238 |
| 收缩率 | |||
| 流动 : 1.00mm | 0.20 | % | |
| 横向流动 : 1.00mm | 0.80 | % | |
| 吸水率 1(平衡,40°C, 95%RH) | 1.6 | % |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | 160 | MPa | ASTM D638 |
| 伸长率 (断裂) | 4.0 | % | ASTM D638 |
| 弯曲模量 | 8500 | MPa | ASTM D790 |
| 弯曲强度 | 205 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 110 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 (1.8 MPa, 未退火) | 290 | °C | ASTM D648 |
| 玻璃转化温度 | 125 | °C | |
| 熔融温度 | 306 | °C |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.0E+16 | ohms·cm | ASTM D257 |
| 介电强度 | 30 | kV/mm | ASTM D149 |
| 介电常数 (10.0 GHz) | 3.30 | ASTM D150 | |
| 耗散因数 (10.0 GHz) | 9.0E-3 | ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | PLC 0 | UL 746 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 | HB | UL 94 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Bar Flow Length 2(320°C,500.0 µm) | 5.30 | cm | |
| Weld Elongation | 0.60 | % | ASTM D638 |
| Weld Strength | 45.0 | MPa | ASTM D638 |
| 备注 | |
|---|---|
| 1 . | 96 hrs |
| 2 . | 750kgf |
PA9T G1300H,日本可乐丽pa9t,高温尼龙 PA9T,增强级pa9t