Petrothene® GA502024
Linear Low Density Polyethylene
LyondellBasell Industries
产品说明：
The Petrothene GA502 series of resins are pelletizedlinear low density polyethylenes for applications re drawdown and toughness. These pelletized products offerexcellent additive homogeneity, require no transfer eion and facilitate clean and safe storage and handling.They can be used in either blown or cast film extrusion. GA502024is formulated with higher antioxidant levels for use in castfilm.
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.918 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 38 | µm | |
| 割线模量 | ASTM D882 | ||
| 1% 正割, MD : 38 µm | 221 | MPa | ASTM D882 |
| 1% 正割, TD : 38 µm | 248 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 38 µm | 33.8 | MPa | ASTM D882 |
| TD : 断裂, 38 µm | 24.8 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 38 µm | 750 | % | ASTM D882 |
| TD : 断裂, 38 µm | 800 | % | ASTM D882 |
| 落锤冲击 (38 µm, 吹塑薄膜) | 120 | g | ASTM D1709A |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 38 µm | 170 | g | ASTM D1922 |
| TD : 38 µm | 400 | g | ASTM D1922 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (45°, 38.1 µm, 吹塑薄膜) | 60 | ASTM D2457 | |
| 雾度 (38.1 µm, 吹塑薄膜) | 12 | % | ASTM D1003 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 熔体温度 | 191 到 218 | °C |