美国NatureWorks Ingeo 6202D PLA
Ingeo™ 6202D
Polylactic Acid
NatureWorks® LLC
产品说明：
NatureWorks® PLA polymer 6202D, a NatureWorks LLCproduct, is a thermoplastic fiber-grade resin derived primarilyfrom annually renewable resources. Available in pellet form, 6202Dis designed for extrusion into mechanically drawn staple fibersusing conventional fiber spinning and drawing equipment.NatureWorks® PLA 6202D can be converted into a broad range of fiberproducts and is recommended for non-dyed fiber applications.
Potential applications for PLA polymer 6202Dinclude:
Fiberfill
Non-wovens
Agricultural woven and nonwoven fabrics
Articles for household disposal
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.24 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (210°C/2.16 kg) | 15 到 30 | g/10 min | ASTM D1238 |
| 收缩性 - Hot Air 1(130°C) | % | ASTM D2102 | |
| 相对粘度 | 3.10 | 内部方法 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 弹性模量 | 30.0 到 40.0 | g/denier | ASTM D2256 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Denier - per filament | > 0.500 | ||
| Elongation of Fibers | 10 到 70 | % | ASTM D2256 |
| Tenacity of Fibers | 2.50 到 5.00 | g/denier | ASTM D2256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 玻璃转化温度 | 55.0 到 60.0 | °C | ASTM D3417 |
| 结晶峰温度 (DSC) | 155 到 170 | °C | ASTM D3418 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 熔体密度 (230°C) | 1.08 | g/cm³ |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 80.0 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 建议的Zui大水分含量 | < 5.0E-3 | % | |
| 熔体温度 | 220 到 240 | °C |