食品级 PCTA 美国伊士曼 DS1910HF NATURAL 耐化学 脱模 成型快薄壁部件
DuraStar™DS1910HF
Thermoplastic Polyester
Eastman Chemical Company
产品说明：
Durastar™ DS1910HF polymer is a high flow grade of Durastar™that contains a mold release. Durastar™ DS1910HF flow lengths areincreased 20-40% relative to Durastar™ DS1010 as shown by spiralflow testing. Other outstanding features of Durastar™ are easilymaintained such as excellent appearance and clarity, good physicalproperties, chemical resistance, and easy processing. This highflow product is especially suited for those applications utilizingthin-walled intricate tools. Under existing United States Food andDrug Administration (FDA) regulations, Durastar™ DS1910HF may beused in food contact articles which comply with the specificationsand conditions of use in 21 CFR 177.1240.
This product is certified to ANSI/NSF Standard 51.
物性信息：
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.19 | g/cm³ | ASTM D792 |
| 收缩率 - 流动 | 0.30 | % | ASTM D955 |
| 吸水率 (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级, 23°C) | 107 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服, 23°C | 50.0 | MPa | ASTM D638 |
| 断裂, 23°C | 43.0 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服, 23°C | 5.0 | % | ASTM D638 |
| 断裂, 23°C | 270 | % | ASTM D638 |
| 弯曲模量 (23°C) | 1900 | MPa | ASTM D790 |
| 弯曲强度 (屈服, 23°C) | 68.0 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -40°C | 44 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 | ASTM D4812 | ||
| -40°C | 无断裂 | ASTM D4812 | |
| 23°C | 无断裂 | ASTM D4812 | |
| 装有测量仪表的落镖冲击 | ASTM D3763 | ||
| -40°C, Energy at PeakLoad | 38.0 | J | ASTM D3763 |
| 23°C, Energy at PeakLoad | 40.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa,未退火 | 73.0 | °C | ASTM D648 |
| 1.8 MPa,未退火 | 66.0 | °C | ASTM D648 |
| 维卡软化温度 | 86.0 | °C | ASTM D1525 1 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 透射率 (总计) | 92.0 | % | ASTM D1003 |
| 雾度 | < 1.0 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 70.0 | °C | |
| 干燥时间 | 4.0 | hr | |
| 加工（熔体）温度 | 230 到 280 | °C | |
| 模具温度 | 15.0 到 30.0 | °C |
| 备注 | |
|---|---|
| 1 . | 压 力1 (10N) |