6.0% 玻璃纤维增强材料
产品说明：
NYCOA 2038 is a 6% glass-fiber reinforced Nylon 6 resinthat offers increased stiffness and dimensional stability. It isformulated to offer outstanding processability, chemicalresistance, and an excellent overall balance of mechanicalproperties.
NYCOA 2038 is available in UV stable, custom colors, and impactmodified grades. In addition, this material has excellent chemicalresistance to greases, oils and other hydrocarbons.
NYCOA 2038 is suitable for general-purpose injection molding, andcan be found in applications that include gears, hardware items,and weed-trimmer parts.
物性信息：
| 基本信息 | |
|---|---|
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.16 | g/cm³ | ASTM D792 |
| 收缩率 | ASTM D955 | ||
| 流动 | 0.80 | % | ASTM D955 |
| 横向流动 | 1.0 | % | ASTM D955 |
| 吸水率 (24 hr) | 1.4 | % | ASTM D570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级) | 120 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 1 | 103 | MPa | ASTM D638 |
| 伸长率 2(断裂) | 10 | % | ASTM D638 |
| 弯曲模量 3 | 3800 | MPa | ASTM D790 |
| 弯曲强度 4 | 140 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 (6.35 mm) | 43 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火 | 200 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 175 | °C | ASTM D648 |
| 熔融温度 | 221 | °C | DSC |
| 补充信息 |
|---|
| The value listed as Melting Point DSC, was tested inaccordance with ASTM D789. |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 71.1 到 82.2 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 料筒后部温度 | 232 到 271 | °C | |
| 料筒中部温度 | 243 到 282 | °C | |
| 料筒前部温度 | 254 到 291 | °C | |
| 射嘴温度 | 252 到 291 | °C | |
| 加工（熔体）温度 | 254 到 291 | °C | |
| 模具温度 | 76.7 到 87.8 | °C | |
| 注射速度 | 快速 | ||
| 背压 | 0.138 到 0.517 | MPa | |
| 垫层 | 1.59 到 6.35 | mm | |
| 螺杆长径比 | 16.0:1.0 | ||
| 螺杆压缩比 | 3.0:1.0 |