增强级 PA66 德国巴斯夫 8231GHS耐碳氢化合物 安全帽 垫圈 高温应用
Ultramid® 8231G HS
Polyamide 6
BASF Corporation
15% 玻璃纤维增强材料
产品说明：
Ultramid 8231G HS is a heat stabilized, 15% glass fiberreinforced PA6 injection molding compound. It is also available innon-heat stabilized (Ultramid 8231) and/or pigmented versions. Theglass fiber reinforcement enhances performance such as strength,stiffness and heat deflection temperature. The heat stabilizersystem extends the properties at elevated temperatures. It also hasexcellent chemical resistance to greases, oils andhydrocarbons.
Applications
Ultramid 8231G HS is ideally suited for more demanding performanceapplications such as safety helmet parts, washers, gears, engineand motor parts, chutes, and higher temperature environments.
物性信息：
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
|
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 比重 | 1.23 | -- | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 0.50 | -- | % | |
| 吸水率 | ||||
| 24hr | 1.4 | -- | % | ASTM D570 |
| 23°C, 24hr | 1.4 | -- | % | ISO 62 |
| 饱和 | 8.1 | -- | % | ASTM D570 |
| 饱和,23°C | 8.1 | -- | % | ISO 62 |
| 平衡, 50%RH | 2.3 | -- | % | ASTM D570 |
| 平衡, 23°C, 50%RH | 2.3 | -- | % | ISO 62 |
| 硬度 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 洛氏硬度 (R 级) | 121 | -- | ASTM D785 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 拉伸模量 | ISO 527-2 | |||
| -40°C | 5950 | 6600 | MPa | ISO 527-2 |
| 23°C | 5960 | 2640 | MPa | ISO 527-2 |
| 80°C | 2470 | 2300 | MPa | ISO 527-2 |
| 121°C | 2090 | 1900 | MPa | ISO 527-2 |
| 抗张强度 | ||||
| 断裂,-40°C | 160 | 170 | MPa | ASTM D638, ISO 527-2 |
| 断裂,23°C | 140 | 79.0 | MPa | ASTM D638 |
| 断裂,80°C | 60.0 | 20.0 | MPa | ASTM D638, ISO 527-2 |
| 断裂,121°C | 50.0 | 40.0 | MPa | ASTM D638, ISO 527-2 |
| 断裂,23°C | 140 | 80.0 | MPa | ISO 527-2 |
| 伸长率 | ||||
| 断裂,-40°C | 3.0 | 4.0 | % | ASTM D638 |
| 断裂,23°C | 4.0 | 9.0 | % | ASTM D638, ISO 527-2 |
| 断裂,80°C | 8.0 | 15 | % | ASTM D638 |
| 断裂,121°C | 7.0 | 6.0 | % | ASTM D638 |
增强级 PA66 德国巴斯夫 8231GHS 耐碳氢化合物安全帽 垫圈 高温应用
增强级 PA66 德国巴斯夫 8231GHS 耐碳氢化合物 安全帽 垫圈高温应用