低翘曲 B3M8 德国巴斯夫 PA6 耐高温 可喷涂 高刚性 可加工 矿物填充40%
Ultramid® B3M8 (8260)
Polyamide 6
BASF Corporation
40% 矿物填料
产品说明：
Ultramid B3M8 (8260) is a 40% mineral reinforced PA6 injectionmolding compound. It possesses high stiffness, dimensionalstability and heat resistance combined with excellentprocessability including low warp and resistance to sink-markformation. It is also available in heat stabilized (Ultramid B3WM8)versions. It can be painted or chrome plated and is also availablein pigmented versions.
物性信息：
| 基本信息 | |
|---|---|
| 填料/增强材料 |
|
| 特性 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 比重 | 1.49 | -- | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 0.90 | -- | % | |
| 吸水率 | ||||
| 24hr | 1.1 | -- | % | ASTM D570 |
| 23°C, 24hr | 1.1 | -- | % | ISO 62 |
| 饱和 | 5.7 | -- | % | ASTM D570 |
| 饱和,23°C | 5.7 | -- | % | ISO 62 |
| 平衡, 50%RH | 1.6 | -- | % | ASTM D570 |
| 平衡, 23°C, 50%RH | 1.6 | -- | % | ISO 62 |
| 硬度 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 洛氏硬度 (R 级) | 119 | -- | ASTM D785 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179 | |||
| -30°C | 3.0 | -- | kJ/m² | ISO 179 |
| 23°C | 3.0 | -- | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度 (23°C) | 120 | -- | kJ/m² | ISO 179 |
| 悬壁梁缺口冲击强度 (23°C) | 53 | -- | J/m | ASTM D256 |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 热变形温度 (0.45 MPa, 未退火) | 195 | -- | °C | ISO 75-2/B |
| 熔融峰值温度 | 220 | -- | °C | ASTM D3418, ISO 3146 |
| 线形热膨胀系数 | ||||
| 流动 | 5.0E-5 | -- | cm/cm/°C | ASTM E831 |
| 流动 | 4.6E-5 | -- | cm/cm/°C | |
| 横向 | 5.8E-5 | -- | cm/cm/°C |
| 电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 体积电阻率 | ||||
| 1.50mm | > 1.0E+15 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| 介电强度 1(1.50mm) | 22 | -- | kV/mm | ASTM D149 |
低翘曲 B3M8 德国巴斯夫 PA6 耐高温 可喷涂 高刚性 可加工 矿物填充40%