PC LEXAN™ EXL1414 沙伯基础 (-40 C) 超韧，耐低温冲击，华南代理

LEXAN™ EXL1414 PC 基础创新塑料(美国)

等级：注塑级 颜色：暂无

特性：易加工性、流动性中等、延展性、共聚物、脱模性能良好

应用领域：电气领域、电子领域、通用

LEXAN™ EXL1414 resin

Polycarbonate

SABIC Innovative Plastics

产品说明：

LEXAN EXL1414 polycarbonate (PC) siloxane copolymer resin is amedium flow opaque injection molding (IM) grade. This resin offersextreme low temperature (-40 C) ductility in combination withexcellent processability and release with opportunities for shorterIM cycle times compared to standard PC. LEXAN EXL1414 resin is aproduct available in wide range of opaque colors and may be anexcellent candidate for a wide variety of applications.

以下是PC(聚碳酸酯)FXE1414T/沙伯基础(SABIC)物性表参数

PROPERTIES TYPICAL VALUESUNITSTEST METHODSFLAMECHARACTERISTICS1)


UL Yellow Card Link
E45329-519321--UL Recognized, 94V-2 Flame Class Rating
≥3mmUL 94UL Recognized, 94HB Flame Class Rating
≥0.4mmUL 94Glow Wire Ignitability Temperature, 3.0 mm
875°CIEC 60695-2-13Glow Wire Ignitability Temperature, 2.5 mm
875°CIEC 60695-2-13Glow Wire Ignitability Temperature, 1.5 mm
875°CIEC 60695-2-13Glow Wire Ignitability Temperature, 1.0 mm
875°CIEC 60695-2-13Glow Wire Ignitability Temperature, 0.8 mm
850°CIEC 60695-2-13Glow Wire Flammability Index, 3.0 mm
960°CIEC 60695-2-12Glow Wire Flammability Index, 2.5 mm
960°CIEC 60695-2-12Glow Wire Flammability Index, 1.5 mm
960°CIEC 60695-2-12Glow Wire Flammability Index, 1.0 mm
960°CIEC 60695-2-12Glow Wire Flammability Index, 0.8 mm
825°CIEC 60695-2-12MECHANICAL



Tensile Stress, yld, Type I, 50 mm/min
57MPaASTM D 638Tensile Stress, brk, Type I, 50 mm/min
59MPaASTM D 638Tensile Strain, yld, Type I, 50 mm/min
5.6%ASTM D 638Tensile Strain, brk, Type I, 50 mm/min
123.9%ASTM D 638Tensile Modulus, 50 mm/min
2180MPaASTM D 638Flexural Stress, yld, 1.3 mm/min, 50 mm span
92MPaASTM D 790Flexural Modulus, 1.3 mm/min, 50 mm span
2180MPaASTM D 790Tensile Stress, yield, 50 mm/min
56MPaISO 527Tensile Stress, break, 50 mm/min
55MPaISO 527Tensile Strain, yield, 50 mm/min
5.4%ISO 527Tensile Strain, break, 50 mm/min
108.5%ISO 527Tensile Modulus, 1 mm/min
2300MPaISO 527Flexural Stress, yield, 2 mm/min
88MPaISO 178Flexural Modulus, 2 mm/min
2120MPaISO 178IMPACT



Izod Impact, notched, 23°C
824J/mASTM D 256Izod Impact, notched, -30°C
712J/mASTM D 256Instrumented Impact Total Energy, 23°C
75JASTM D 3763Izod Impact, unnotched 80*10*3 +23°C
NBkJ/m²ISO 180/1UIzod Impact, unnotched 80*10*3 -30°C
NBkJ/m²ISO 180/1UIzod Impact, notched 80*10*3 +23°C
65kJ/m²ISO 180/1AIzod Impact, notched 80*10*3 -30°C
55kJ/m²ISO 180/1ACharpy 23°C, V-notch Edgew 80*10*3 sp=62mm
70kJ/m²ISO 179/1eACharpy -30°C, V-notch Edgew 80*10*3 sp=62mm
60kJ/m²ISO 179/1eACharpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
NBkJ/m²ISO 179/1eUCharpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
NBkJ/m²ISO 179/1eUTHERMAL



Vicat Softening Temp, Rate A/50
138°CASTM D 1525HDT, 1.82 MPa, 3.2mm, unannealed
120°CASTM D 648CTE, -40°C to 95°C, flow
6.7E-051/°CASTM E 831CTE, -40°C to 95°C, xflow
8.E-051/°CASTM E 831CTE, 23°C to 80°C, flow
6.7E-051/°CISO 11359-2CTE, 23°C to 80°C, xflow
8.E-051/°CISO 11359-2Ball Pressure Test, 125°C +/- 2°C
pass-IEC 60695-10-2Vicat Softening Temp, Rate B/50
138°CISO 306Vicat Softening Temp, Rate B/120
139°CISO 306HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
118°CISO 75/AfRelative Temp Index, Elec1)130°CUL 746BRelative TempIndex, Mech w/impact1)120°CUL 746BRelative Temp Index, Mech w/oimpact1)130°CUL 746BPHYSICAL



Specific Gravity
1.19-ASTM D 792Mold Shrinkage, flow, 3.2 mm
0.4-0.8%SABIC methodMelt Flow Rate, 300°C/1.2 kgf
10g/10 minASTM D 1238Density
1.19g/cm³ISO 1183Water Absorption, (23°C/saturated)
0.13%ISO 62-1Moisture Absorption (23°C / 50% RH)
0.09%ISO 62Melt Volume Rate, MVR at 300°C/1.2 kg
9cm³/10 minISO 1133ELECTRICAL



Comparative Tracking Index (UL) {PLC}
3PLC CodeUL 746AHot-Wire Ignition (HWI), PLC 2
≥3mmUL 746AHot-Wire Ignition (HWI), PLC 3
≥1.5mmUL 746AHigh Amp Arc Ignition (HAI), PLC 1
≥1.5mmUL 746AInjection Molding



Drying Temperature
120°C
Drying Time
3-4hrs
Drying Time (Cumulative)
48hrs
Maximum Moisture Content
0.02%
Melt Temperature
295-315°C
Nozzle Temperature
290-310°C
Front - Zone 3 Temperature
295-315°C
Middle - Zone 2 Temperature
280-305°C
Rear - Zone 1 Temperature
270-295°C
Mold Temperature
70-95°C
Back Pressure
0.3-0.7MPa
Screw Speed
40-70rpm
Shot to Cylinder Size
40-60%
Vent Depth
0.025-0.076mm

PC树脂具有独特的综合特性，适合诸多市场的不同应用，包括照明、医疗、消费电子产品和电器等，可在透明度、耐热性和耐冲击性之间实现搭配。它们可以提供不同的熔融流率与色调，并且可以使用添加剂进行改性，以提高特定的性能特性，包括阻燃性、耐紫外安定性、挺度、透光度、颜色以及脱模性能，使用专有生产工艺进行生产，使材料能够在较宽的温度范围内保持极高的延展性和韧性，PC产品具备玻璃的透明度、橡胶的弹性和触感、钢材的强度以及铝材的轻质优势。PC塑料具有绝缘和抗紫外线特性，专为美观、安全、坚固且耐久的应用而设计。比如在建筑领域，建筑师、工程师和建筑拥有人一直寻找在一些方法，即可在无需影响风格的前提下，提升结构和标牌的安全性、强度和可持续性。能效和可持续性的目标继续驱动建筑施工行业中更严格的监管、实践和创新。并且具有前瞻思维，为您将来对高质量、节能建材产品的需求进行设想和规划。这样一来PC成为了理想的选择，PC建筑领域主要应用包括；透明屋顶和玻璃门窗，工业标牌和道路标线飓风挡风板隔热，卫生浴缸衬垫和淋浴盆，窗框和配件，用于地下/墙内管道、水龙头和配件的密封剂，污水系统检查室，用于屋顶下表面、通风系统和烟囱的绝缘密封系统.