Celcon®CF802
Acetal (POM) Copolymer
Celanese Corporation
产品说明：
Celcon® acetal copolymer grade CF802 is a conductive, fuelcompatible general purpose acetal copolymer. Celcon® CF802 has beendeveloped to dissipate static electricity from fuel handlingsystems.
Please note Celcon® CF802 has special processing considerations toensure static dissipation properties. Use minimum back pressure andslowest screw speed possible in retracting screw during coolingportion of cycle. Large gate size (>2 mm) recommended. Pneumaticconveying of material long distances is not recommended.
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 多点数据 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.47 | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 | 1.6 | % | ISO 294-4 |
| 流动方向 | 1.7 | % | ISO 294-4 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 3000 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 62.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 10 | % | ISO 527-2/1A/50 |
| 拉伸蠕变模量 | ISO 899-1 | ||
| 1 hr | 2130 | MPa | ISO 899-1 |
| 1000 hr | 1050 | MPa | ISO 899-1 |
| 弯曲模量 (23°C) | 3100 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | ||
| -30°C | 70 | kJ/m² | ISO 179/1eU |
| 23°C | 70 | kJ/m² | ISO 179/1eU |
| 悬壁梁缺口冲击强度 (23°C) | 4.8 | kJ/m² | ISO 180/1A |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 (1.8 MPa, 未退火) | 100 | °C | ISO 75-2/A |
| 熔融温度 1 | 167 | °C | ISO 11357-3 |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动 | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| 横向 | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表面电阻率 | 2.0E+3 | ohms | IEC 60093 |
| 体积电阻率 | |||
| -- | 1.0E+3 | ohms·cm | ASTM D257 |
| -- | 3.0E+2 | ohms·cm | IEC 60093 |