SABICInnovative Plastics NORYL N225X PPE+PS
Polystyrene (PS)
SABIC Innovative Plastics (GE Plastics)
产品说明：
PPE+PS blend. Unfilled. Halogen-Free FR performance. UL94V0/5VA. UL746C F1. Dielectric Strength. Suitable for E/E marketindoor/outdoor applications.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 17 % | 17 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 8.0 % | 8.0 % | Type I, 50 mm/min; ASTM D638 |
| 弯曲强度 | 99.0 MPa | 14400 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 弯曲模量 | 2.49 GPa | 361 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.86 J/cm | 3.48 ft-lb/in | ASTM D256 |
| 0.960 J/cm @Temperature -30.0 °C | 1.80 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 8.86 J/cm @Thickness 3.20 mm | 16.6 ft-lb/in @Thickness 0.126 in | ASTM D256 | |
| 落锤总能量 | 39.0 J | 28.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 11.0 J @Temperature -30.0 °C | 8.11 ft-lb @Temperature -22.0 °F | Instrumented Impact Energy @ peak; ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 2.80e+16 ohm-cm | 2.80e+16 ohm-cm | ASTM D257 |
| 表面电阻 | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| 介电常数 | 2.55 @Frequency 1.00e+6 Hz | 2.55 @Frequency 1.00e+6 Hz | ASTM D150 |
| 2.69 @Frequency 50.0 - 60.0 Hz | 2.69 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
| 介电强度 | 16.2 kV/mm @Thickness 3.20 mm | 411 kV/in @Thickness 0.126 in | in oil; ASTM D149 |
| 耗散因数 | 0.0070 @Frequency 1.00e+6 Hz | 0.0070 @Frequency 1.00e+6 Hz | ASTM D150 |
| 0.010 @Frequency 50.0 - 60.0 Hz | 0.010 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
| 耐电弧性 | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | UL 746A |
| 热丝引燃 (HWI) | 60 - 120 sec | 60 - 120 sec | UL 746A |
| 高电弧燃烧，HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 109 °C @Thickness 6.40 mm | 228 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 99.0 °C @Thickness 6.40 mm | 210 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| 维卡软化温度 | 128 °C | 262 °F | Rate B/50; ASTM D1525 |
| UL RTI | 95.0 °C | 203 °F | UL 746B |
| UL RTI，机械冲击 | 80.0 °C | 176 °F | UL 746B |
| UL RTI，机械无冲击 | 95.0 °C | 203 °F | UL 746B |
| 可燃性(UL94) | HB @Thickness 0.400 mm | HB @Thickness 0.0157 in | UL 94 |
| V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | UL 94 | |
| 5VA @Thickness 2.99 mm | 5VA @Thickness 0.118 in | UL 9 |