KraiburgTPE THERMOLAST® K TC7MGA Natural TPE
Styrenic TPE
Kraiburg TPE
产品说明：
Adhesion to technical thermoplastics
Adhesion to ABS, SAN, ASA, PC, PC/ABS, PC/PBT, PBT, PET, PETG,PMMA
For patent free comolded parts
Good flow characteristics
Excellent adhesion even with soft compounds
UL94 HB listed compounds available
Typical Applications:
Electric and electronic components
Seals
Coverings
Design and functional elements
Handles (for hand tools, power tools, etc.)
In the automotive industry (air inlet piping, cowl, stop button,door sill, etc.)
Material Advantages:
Excellent adhesion without pretreatment (depending on geometryand processing)
Adhesion to many engineering thermoplastics
Easy to color
Tactile surface (soft touch)
Excellent flow characteristics
Processing:
Processing on 2K injection molding machines (many grades alsofor insert molding)
Low back pressure
High shear force is beneficial for flow behavior
High injection speed and pressure
Information provided by Kraiburg TPE.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.18 g/cc | 0.0426 lb/in³ | DIN 53479 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | 77 | 77 | DIN 53505 |
| 抗张强度(断裂) | 7.40 MPa | 1070 psi | DIN 53504 |
| 伸长率 (断裂) | 550 % | 550 % | DIN 53504 |
| 撕裂强度 | 29.6 kN/m | 169 pli | DIN 53515 |
| 压缩 | 30 % | 30 % | 72 hours at 23°C, preliminary value; ISO 815 |
| 65 % @Temperature 70.0 °C | 65 % @Temperature 158 °F | 24 hours at 70°C, preliminary value; ISO 815 | |
| 80 % @Temperature 100 °C | 80 % @Temperature 212 °F | 24 hours at 100°C, preliminary value; ISO 815 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工温度 | 180 - 240 °C | 356 - 464 °F | |
| 模具温度 | 40.0 - 60.0 °C | 104 - 140 °F | |
| 干燥温度 | 60.0 - 80.0 °C | 140 - 176 °F | Pre-drying |
| 干燥时间 | 2 - 4 hour | 2 - 4 hour | Pre-drying |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | Natural |