现货销售 INFUSE™ 美国陶氏 OBC 9000 回弹性 抗撕裂 耐候 家居用品造型材
INFUSE™9000
Olefin Block Copolymer
陶氏塑料
产品说明：
INFUSE™ 9000 Olefin Block Copolymer is a high performance olefinblock copolymer that can be widely used in thermoplastic elastomerapplications where higher service temperature re areneeded.
INFUSE 9000 also provides high filler loading capability along withlow compression set and good processability.
Main Characteristics:
High upper service temperature performance
Highly flexible with good elastic recovery
Fast set up times for processability
General purpose elastomer
Excellent for compounds and blends
Complies with
EU, No 10/2011
U.S. FDA FCN 424
Consult the regulations for complete details.
物性信息：
| 基本信息 | |
|---|---|
| 机构评级 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.877 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A, 模压成型) | 71 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 - 正割 (模压成型) | 3.29 | MPa | ASTM D638 |
| 抗张强度 (断裂, 模压成型) | 6.28 | MPa | ASTM D638 |
| 伸长率 (断裂, 模压成型) | 370 | % | ASTM D638 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (断裂) | 15.0 | MPa | ASTM D412 |
| 伸长率 (断裂) | 1200 | % | ASTM D412 |
| 撕裂强度 | 42.0 | kN/m | ASTM D624 |
| 压缩yongjiu变形 | ASTM D395 | ||
| 23°C | 23 | % | ASTM D395 |
| 70°C | 45 | % | ASTM D395 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 溶融温度（DSC） | 120 | °C | 内部方法 |
| TMA 1(1.00mm) | 104 | °C | 内部方法 |
现货销售 INFUSE™ 美国陶氏 OBC 9000 回弹性 抗撕裂 耐候 家居用品造型材