SABIC V01550 PPE+HIPS
SABIC Innovative Plastics (GE Plastics)
产品说明：
NORYL V01550 is a 15 % short glass fibre reinforced, flameretardant material with a HDT/A of 130C according ISO 75. NORYLV01550 is V0 at 0.75 mm according UL94 and is halogen freeaccording VDE/DIN 472 part 815. NORYL V01550 is designed forelectronic and electrical applications.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| 水分吸收 | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.50 % | 0.50 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C | 7.0 g/10 min @Load 11.0 lb, Temperature 536 °F | MVR [cm^3/10 min]; ISO 1133 |
| 10 g/10 min @Load 5.00 kg, Temperature 300 °C | 10 g/10 min @Load 11.0 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 硬度，H358/30 | 130 MPa | 18900 psi | ISO 2039-1 |
| 抗张强度(断裂) | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 伸长率 (断裂) | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 拉伸模量 | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 |
| 弯曲强度 | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| 弯曲模量 | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| 悬壁梁无缺口冲击强度 | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| 45.0 kJ/m² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| 简支梁无缺口冲击强度 | 4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 4.50 J/cm² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 泰伯磨损，毫克/1000次 | 50 | 50 | CS-17, 1 kg; SABIC Method |