LEXAN™ PC 基础创新(美国) 201R-111 聚碳酸酯 现货

LEXAN™ 201R resin

物性信息：

硬度额定值单位制测试方法洛氏硬度

ASTM D785    M级70
ASTM D785    R级118
ASTM D785 机械性能额定值单位制测试方法抗张强度 1

ASTM D638    屈服62.1MPaASTMD638    断裂68.9MPaASTM D638伸长率 2

ASTM D638    屈服7.0%ASTMD638    断裂140%ASTMD638弯曲模量 3(50.0 mm跨距)2340MPaASTM D790弯曲强度 4(屈服, 50.0 mm 跨距)97.9MPaASTMD790泰伯耐磨性 (1000 Cycles, 1000 g, CS-17转轮)10.0mgASTM D1044冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 (23°C)910J/mASTM D256无缺口悬臂梁冲击 (23°C)3200J/mASTMD4812装有测量仪表的落镖冲击 (23°C, Energy at PeakLoad)65.0JASTM D3763落锤冲击 (23°C)169JASTMD3029拉伸冲击强度 5630kJ/m²ASTMD1822热性能额定值单位制测试方法载荷下热变形温度

ASTM D648    0.45 MPa,未退火, 6.40 mm138°CASTMD648    1.8 MPa, 未退火,6.40 mm132°CASTM D648维卡软化温度154°CASTMD1525 6线形热膨胀系数 - 流动 (-40 到 95°C)6.8E-5cm/cm/°CASTME831比热1260J/kg/°CASTM C351导热系数0.29W/m/KASTM C177RTI Elec130°CUL746RTI Imp130°CUL 746RTI130°CUL 746电气性能额定值单位制测试方法体积电阻率>1.0E+17ohms·cmASTM D257介电强度 (3.20 mm, inAir)15kV/mmASTM D149介电常数

ASTM D150    50Hz3.17
ASTM D150    60Hz3.17
ASTM D150    1MHz2.96
ASTM D150耗散因数

ASTM D150    50Hz9.0E-4
ASTM D150    60Hz9.0E-4
ASTM D150    1MHz0.010
ASTM D150相比耐漏电起痕指数(CTI)PLC 2
UL 746高电弧燃烧指数(HAI)PLC 1
UL 746高电压电弧起痕速率 (HVTR)PLC 2
UL 746热丝引燃 (HWI)PLC 2
UL 746可燃性额定值单位制测试方法UL 阻燃等级

UL 94    1.09mmV-2
UL 94    5.99mmV-0
UL 94光学性能额定值单位制测试方法折射率1.586
ASTM D542透射率 (2540 µm)88.0%ASTMD1003雾度 (2540 µm)1.0%ASTMD1003注射额定值单位制
干燥温度121°C
干燥时间3.0 到 4.0hr
干燥时间48hr
建议的水分含量0.020%
建议注射量40 到 60%
料筒后部温度288 到 310°C
料筒中部温度299 到 321°C
料筒前部温度310 到 332°C
射嘴温度304 到 327°C
加工（熔体）温度310 到 332°C
模具温度82.2 到 116°C
背压0.345 到 0.689MPa
螺杆转速40 到 70rpm
排气孔深度0.025 到 0.076mm
基本信息
黄卡编号

E121562-220871

特性

阻燃性

加工方法

注射成型

物理性能额定值单位制测试方法比重

ASTM D792    --1.20g/cm³ASTMD792    --1.19g/cm³ASTM D792特定体积0.835cm³/gASTMD792熔流率（熔体流动速率） (300°C/1.2kg)7.0g/10 minASTM D1238收缩率 - 流动 (3.20 mm)0.50 到 0.70%内部方法吸水率

ASTM D570    24hr0.15%ASTM D570    平衡, 23°C0.35%ASTMD570    平衡,100°C0.58%ASTM D570室外适用性f2
UL 746C