C63000铜合金
【铝青铜C63000产品简介】
******************************************
镍铝铁青铜,其独特的综合性能的高强度,良好的疲劳,优良的耐腐蚀性能,
它有非常高的抗磨损性能。
化学成分表：
Element | Cu | Al | Ni+Co | Fe | Mn | Si | Sn | Zn |
% | Bal | 9.0-11.0 | 4.0-5.5 | 2.0-4.0 | 1.5max | 0.25max | 0.2max | 0.3max |
机械性能表：
Form | SizeRange | Yield0.2% | UTS | Elong% | Hardness(HB) | |||
Metric | Imperial | MPa | Ksi | MPa | Ksi | % | (HB) | |
020 | 75-300mmdia | 3-12” dia | 300-350 | 43.5-50.7 | 600-700 | 87-101 | 12-21 | 180-240 |
HR50 | 50-80 mmdia | 2.0-3.2” dia | 380-430 | 62.3-62.3 | 725-800 | 105-116 | 10-15 | 180-240 |
TQ50 | 80-130 mmdia | 3.2–5.1” dia | 320-400 | 46.4-58.0 | 620-770 | 90-111.7 | 15-20 | 180-240 |
020–Hotforged and annealed, HR50 Drawn and Stress relieved (High Strength)TQ50 Quench hardened and temper annealed.
物理性质AMS 4640
密度- 0.274磅/ in3在68 F
特定的重力- 7.58
电阻率- 116.0 ohms-cmil/英尺@ 68 F
导电率- 7% IACS @ 68 F
镍铝青铜的典型使用AMS 4640
-阀茎、泵轴、密封腺体,防喷器部分
,起落架衬套及轴承、皮瓣衬套,致动器,部分,支撑套管
汽车气门,气门座
其他工业——球、齿轮、凸轮、轴系、发电站的冷凝器管和脱盐装置,气门座,气门,泵轴、结构成员,、热交换器、头,换热器法兰、轴承、轴套、阀球,液压衬套为地球移动设备、耐腐蚀的文章,飞机零件、焊接管
它们是QAl5、QAl7、QAl9-2、QAl9-4、QAl9-5-1-1、QAl10-3-1.5、QAl10-4-4、QAl10-5-5、QAl11-6-6.而美国ASTM标准中加工铝青铜共有26，铸造合金有18个。铝青铜的基本合金组成为Cu-Al、Cu-Al-Fe、Cu-Al-Ni、Cu-Al-Fe-Ni、Cu-Al-Fe-Ni-Mn等。
公司常年备现货库存。欢迎各界人士莅临参观指导！！！
UNS No. C95200; UNS No. CuAl10Fe5Ni5-C; UNS No. CuAl10Fe5Ni5-C;UNS No. C95410; UNS No. C95500; UNS No. CuAl10Fe5Ni5-C; UNS No.C95600; UNS No. C95700; UNS No. CuAl10Fe5Ni5-C; UNS No. C95820; andUNS No. C95900.
(In Tension)
Imperial | Metric | |
Density | 0.274lb/in³@ 68º F | 7580kg/m³ @20ºC |
SpecificGravity | 7.58 | 7.58 |
SpecificHeat | 0.090Btu/lb º F @68ºF | 376.7 J/kgºC@20 ºC |
ElectricalConductivity | 7% IACS @68º F | 0.041megaSiemens/cm @20 ºC |
ThermalConductivity | 22.6Btu.ft(hr.ft² º F) @68ºF | 0.391W/cmºC@20 ºC |
ThermalExpansion | 9.0x10ˉ 6 per º F(68-572 º F ) | 15.5x10ˉ 6 perºC (20-300ºC) |
ElectricalResistivity | 116Ω-cmil/ft@ 68º F | 19.28 µΩ-cm@20ºC |
Relative MagneticPermeability | 1.4µ | |
MachiningIndex | 20 (Based on freemachining brass ) | |
Modulus ofRigidity | 6800ksi | 46884MPa |
Modulus ofElasticity | 18200ksi | 125484MPa |
MeltingRange | 1920-1960ºF | 1049-1071ºC |
Hot WorkingRange | 1450-1700ºF | 788-927ºC |
ColdWorking | Limited | |
Cryogenic | Retainsproperties down to – 302ºF | (-190ºC) |
ElevatedTemperatures | Retainsproperties to 662 ºF | (350ºC) |