LG Chemical AF312T ABS物性表
物理性能额定值 (公制)额定值 (英制)测试方法比重1.18 g/cc1.18 g/ccASTMD792处理0.0100.010Injection Molding线性成型收缩率,Flow0.0040 - 0.0070 cm/cm@Thickness 3.20 mm
0.0040 - 0.0070 in/in@Thickness 0.126 in
ASTM D955熔体流动速率52 g/10 min@Load 10.0 kg, Temperature 220 °C
52 g/10 min@Load 22.0 lb, Temperature 428 °F
ASTM D1238机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度(R 级)104104ASTMD785抗张强度(屈服)42.2 MPa@Thickness 3.20 mm
6120 psi@Thickness 0.126 in
50 mm/min; ASTM D638伸长率 (断裂)25 %@Thickness 3.20 mm
25 %@Thickness 0.126 in
50 mm/min; ASTM D638屈服伸长率>= 5.0 %@Thickness 3.20 mm
>= 5.0 %@Thickness 0.126 in
50 mm/min; ASTM D638拉伸模量2.16 GPa@Thickness 3.20 mm
313 ksi@Thickness 0.126 in
1 mm/min; ASTM D638弯曲强度68.6 MPa@Thickness 6.40 mm
9960 psi@Thickness 0.252 in
15 mm/min; ASTM D790弯曲模量2.60 GPa@Thickness 6.40 mm
377 ksi@Thickness 0.252 in
15 mm/min; ASTM D790悬壁梁缺口冲击强度2.26 J/cm@Thickness 6.40 mm, Temperature 23.0 °C
4.22 ft-lb/in@Thickness 0.252 in, Temperature 73.4 °F
ASTM D2562.75 J/cm
@Thickness 3.20 mm, Temperature 23.0 °C
5.14 ft-lb/in@Thickness 0.126 in, Temperature 73.4 °F
ASTM D256Izod Impact, Unnotched0.785 J/cm@Thickness 6.40 mm, Temperature -30.0 °C
1.47 ft-lb/in@Thickness 0.252 in, Temperature -22.0 °F
ASTM D2560.785 J/cm
@Thickness 3.20 mm, Temperature -30.0 °C
1.47 ft-lb/in@Thickness 0.126 in, Temperature -22.0 °F
ASTM D256电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率1.00e+14 ohm-cm1.00e+14ohm-cm介电强度30.0 kV/mm762 kV/in
相比耐漏电起痕指数(CTI)400 - 600 V400 - 600 V
热丝引燃 (HWI)15 - 30 sec
@Thickness >=1.50 mm
15 - 30 sec@Thickness >=0.0591 in
15 - 30 sec
@Thickness >=2.00 mm
15 - 30 sec@Thickness >=0.0787 in
15 - 30 sec
@Thickness >=2.50 mm
15 - 30 sec@Thickness >=0.0984 in
60 - 120 sec
@Thickness >=3.00 mm
60 - 120 sec@Thickness >=0.118 in
高电弧燃烧指数(HAI)>= 120 arcs
@Thickness 1.50 mm
>= 120 arcs@Thickness 0.0591 in
>= 120 arcs
@Thickness 2.00 mm
>= 120 arcs@Thickness 0.0787 in
>= 120 arcs
@Thickness 2.50 mm
>= 120 arcs@Thickness 0.0984 in
>= 120 arcs
@Thickness 3.00 mm
>= 120 arcs@Thickness 0.118 in
高压电弧跟踪率,HVTR25.4 - 50.0 mm/min1.00 - 1.97 in/min
热性能额定值 (公制)额定值 (英制)测试方法载荷下热变形温度(0.46 MPa)84.0 °C
@Thickness 6.40 mm
183 °F@Thickness 0.252 in
Unannealed; ASTM D648载荷下热变形温度(1.8 MPa)76.0 °C@Thickness 6.40 mm
169 °F@Thickness 0.252 in
Unannealed; ASTM D648维卡软化温度84.0 °C@Load 5.00 kg
183 °F@Load 11.0 lb
50°C/h; ASTM D1525UL RTI85.0 °C@Thickness >=1.50 mm
185 °F@Thickness >=0.0591 in
UL 746B85.0 °C
@Thickness >=2.00 mm
185 °F@Thickness >=0.0787 in
85.0 °C
@Thickness >=2.50 mm
185 °F@Thickness >=0.0984 in
85.0 °C
@Thickness >=3.00 mm
185 °F@Thickness >=0.118 in
UL RTI,机械冲击75.0 °C
@Thickness >=1.50 mm
167 °F@Thickness >=0.0591 in
UL 746B75.0 °C
@Thickness >=2.00 mm
167 °F@Thickness >=0.0787 in
75.0 °C
@Thickness >=2.50 mm
167 °F@Thickness >=0.0984 in
75.0 °C
@Thickness >=3.00 mm
167 °F@Thickness >=0.118 in
UL RTI,机械无冲击75.0 °C
@Thickness >=1.50 mm
167 °F@Thickness >=0.0591 in
UL 746B75.0 °C
@Thickness >=2.00 mm
167 °F@Thickness >=0.0787 in
75.0 °C
@Thickness >=2.50 mm
167 °F@Thickness >=0.0984 in
75.0 °C
@Thickness >=3.00 mm
167 °F@Thickness >=0.118 in
可燃性(UL94)V-0
@Thickness >=1.50 mm
V-0@Thickness >=0.0591 in
V-0
@Thickness >=2.00 mm
V-0@Thickness >=0.0787 in
V-0
@Thickness >=2.50 mm
V-0@Thickness >=0.0984 in
V-0
@Thickness >=3.00 mm
V-0@Thickness >=0.118 in
加工性能额定值 (公制)额定值 (英制)测试方法料筒后部温度170 - 190 °C338 - 374 °FInjectionMolding料筒中部温度180 - 200 °C356 - 392 °FInjection Molding料筒前部温度190 -210 °C374 - 410 °FInjection Molding射嘴温度200 - 230 °C392 - 446°FInjection Molding加工(熔体)温度200 - 230 °C392 - 446 °FInjectionMolding模具温度40.0 - 60.0 °C104 - 140 °FInjection Molding干燥温度70.0 -80.0 °C158 - 176 °FInjection Molding干燥时间2.00 - 4.00 hour2.00 - 4.00hourInjection Molding背压0.490 - 0.981 MPa71.1 - 142 psiInjectionMolding螺杆转速30 - 60 rpm30 - 60 rpmInjection Molding