原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D792 | 1.17 | 23度比重 | |
| 24小时吸水率 | ASTM D570 | 0.30 | % | ||
| 熔流率 | ASTM D1238 | 10 | g/10 min | ||
| 收缩率 | 平行流动方向 | ASTM D955 | 0.0030 - 0.0060 | cm/cm | |
| 机械性能 | 抗压强度 | ASTM D695 | 72.4 | MPa | |
| 拉伸模量 | ASTM D638 | 2280 | MPa | ||
| 断裂点拉伸强度 | ASTM D638 | 41.4 | MPa | ||
| 弯曲模量 | ASTM D790 | 2450 | MPa | ||
| 屈服点弯曲强度 | ASTM D790 | 85.5 | MPa | ||
| 断裂点伸长率 | ASTM D638 | 25 | % | ||
| 缺口冲击强度 | ASTM D256 | 32.0 | J/m | ||
| 热性能 | 热传导 | ASTM C177 | -- | W/m/K | |
| 维卡软化温度 | Rate A, Loading 1 (10 N) | ASTM D1525 | 84.4 | ℃ | |
| 热变形温度 | 264 psi，未退火 | ASTM D648 | 81.7 | ℃ | |
| UL阻燃等级 | 1.47 mm | UL 94 | HB | ||
| 光学性能 | 折射率 | ASTM D542 | 1.490 | ||
| 透光度 | ASTM D1003 | 92.0 | % | ||
| 雾度 | ASTM D1003 | 2.0 | % | ||