XENOY™ 1103BK 1066 resin
聚碳酸酯+PBT
SABIC Innovative Plastics
产品说明:
AUTOMOTIVE. Unreinforced, impact modified PBT+PC alloy.Excellent low temperature impact and chemical resistance. Rangegray, black colors.
![11321875.jpg](//static.11467.com/img/lazy.gif)
基本信息 |
|
---|
黄卡编号 | |
添加剂 | |
特性 | |
用途 | |
外观 | |
加工方法 | |
多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Compressive Stress vs. Strain (ASTM D695) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|
比重 | 1.20 | g/cm³ | ASTM D792 |
熔流率(熔体流动速率) (250°C/5.0 kg) | 13 | g/10 min | ASTM D1238 |
收缩率 - 流动 (3.20 mm) | 0.80 到 1.0 | % | 内部方法 |