沙伯基础PC/ABS C1100HF物性参数

SABIC Innovative Plastics Cycoloy® C1100HF PC+ABS(Europe-Africa-Middle East) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.12 g/cc0.0405 lb/in³ISO 1183平衡吸湿0.20%0.20 %23°C / 50% RH; ISO 62饱和吸水率0.60 %

@Temperature 23.0 °C

0.60 %

@Temperature 73.4 °F

ISO 62线性成型收缩率,Flow0.0050 - 0.0070 cm/cm0.0050 - 0.0070 in/inontensile bar; SABIC Method熔体流动速率6.0 g/10 min

@Load 2.16 kg, Temperature 260 °C

6.0 g/10 min

@Load 4.76 lb, Temperature 500 °F

[cm^3/10 min] Melt Volume Rate; ISO 1133
20 g/10 min

@Load 5.00 kg, Temperature 260 °C

20 g/10 min

@Load 11.0 lb, Temperature 500 °F

[cm^3/10 min] Melt Volume Rate; ISO 1133机械性能额定值 (公制)额定值(英制)测试方法洛氏硬度（R 级）117117ISO 2039-2硬度，H358/3099.0 MPa14400 psiISO2039-1抗张强度(断裂)45.0 MPa6530 psi5 mm/min; ISO 527
45.0 MPa6530 psi50 mm/min; ISO 527抗张强度(屈服)55.0 MPa7980 psi5 mm/min;ISO 527
55.0 MPa7980 psi50 mm/min; ISO 527伸长率 (断裂)>= 50 %>= 50 %50mm/min; ISO 527
120 %120 %5 mm/min; ISO 527屈服伸长率4.0 %4.0 %50 mm/min; ISO 527
5.0 %5.0 %5 mm/min; ISO 527拉伸模量2.40 GPa348 ksi1 mm/min; ISO527弯曲强度75.0 MPa10900 psi2 mm/min; ISO 178弯曲模量2.30 GPa334 ksi2mm/min; ISO 178悬壁梁缺口冲击强度25.0 kJ/m²

@Temperature -30.0 °C

11.9 ft-lb/in²

@Temperature -22.0 °F

80*10*3; ISO 180/1A
28.0 kJ/m²

@Temperature -30.0 °C

13.3 ft-lb/in²

@Temperature -22.0 °F

80*10*4; ISO 180/1A
50.0 kJ/m²

@Temperature 23.0 °C

23.8 ft-lb/in²

@Temperature 73.4 °F

80*10*3; ISO 180/1A悬壁梁无缺口冲击强度NB

@Temperature 23.0 °C

NB

@Temperature 73.4 °F

80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C

NB

@Temperature -22.0 °F

80*10*4; ISO 180/1U简支梁缺口冲击强度2.50 J/cm²

@Temperature -30.0 °C

V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
3.00 J/cm²

@Temperature -30.0 °C

14.3 ft-lb/in²

@Temperature -22.0 °F

V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
5.00 J/cm²

@Temperature 23.0 °C

V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
5.50 J/cm²

@Temperature 23.0 °C

26.2 ft-lb/in²

@Temperature 73.4 °F

V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA泰伯磨损，毫克/1000次81

@Load 1.00 kg

81

@Load 2.20 lb

CS-17; SABIC Method