| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 弯曲强度 | 11200 | lb/in | ASTM D-790 |
| 弯曲弹性率 | 3.8×10 | lb/in | ASTM D-790 |
| 引张强度 | ASTM D-638 | ||
| 480 | kg/cm | ||
| 6800 | lb/in | ||
| IZOD冲击强度 (1/8") | 3.7 | ft.lb/in | ASTM D-256 |
| 弯曲弹性率 | 2.7×10 | kg/cm | ASTM D-790 |
| 弯曲强度 | 790 | kg/cm | ASTM D-790 |
| 洛氏硬度 | 116 | R | ASTM D-785 |
| IZOD冲击强度 | ASTM D-256 | ||
| (1/4") | 18 | kg.cm/cm | |
| (1/4") | 3.3 | ft.lb/in | |
| (1/8") | 20 | kg.cm/cm | |
| 伸长率 | 20 | % | ASTM D-638 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 热变形温度 | 88(190) | ℉ | ASTM D-648 |
| 维卡软化点 | 105 | ℃ | ASTM D-1525 |
| 燃烧性 (File No. E56070 UL&C-UL) | 1/16"HB | ||
| 维卡软化点 | 221 | ℉ | ASTM D-1525 |
| 热变形温度 | 99(210) | ℃ | ASTM D-648 |
| 熔体流动速率 | ASTM D-1238 | ||
| (220℃×10kg) | 22 | g/10min | |
| (200℃×5kg) | 1.8 | g/10min | |
| 比重 | 1.05 | 23/23℃ | ASTM D-792 |