产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 比重 | ASTM D-792 | 1.21 | g/cm3; | |
| ISO 1183 2 | 1210 | kg/m3; | |||
| 收缩率 | 流动 2.54 mm | ASTM D-955 | 0.80 | % | |
| 横向流动 2.54 mm | ASTM D-955 | 0.80 | % | ||
| 硬度计硬度 | 支撐 D | ASTM D-2240 | 55 | ||
| 机械性能 | 拉伸应力 | 50%应变 | ISO 527-2 2 | 12.0 | MPa |
| 拉伸应变 | 断裂 | ISO 527-2 2 | > 50 | % | |
| 弯曲模量 | 23°C | ASTM D-790 | 138 | MPa | |
| 抗泰伯磨耗 | 1000 Cycles, 1000 g, H-18 转轮 | ASTM D-1044 | 50.0 | mg | |
| 剪切强度 | ASTM D-732 | 38.5 | MPa | ||
| 拉伸应力 | 50%应变 | ASTM D-412 | 12.4 | MPa | |
| 应变 | ASTM D-412 | 13.8 | MPa | ||
| 300%应变 | ASTM D-412 | 27.6 | MPa | ||
| 抗张强度 | 屈服 | ASTM D-412 | 41.4 | MPa | |
| 伸长率 | 屈服 | ASTM D-412 | 500 | % | |
| 撕裂强度 | ASTM D-624 | 158 | kN/m | ||
| 压缩变形 | 23℃, 22.0 hr | ASTM D-395 | 20 | % | |
| 巴肖氏弹性 | ASTM D-2632 | 40 | % | ||
| 装有测量仪表的落镖冲击 | -30°C, 2.54 mm, Total Energy | ASTM D3763 | 50.0 | J | |
| 23°C, 2.54 mm, Total Energy | ASTM D3763 | 57.8 | J | ||
热性能 | 热变形温度 | 0.45 MPa, 未退火 | ASTM D-648 | 59.4 | ℃ |
| 0.45 MPa | ASTM D-648 | 59.0 | ℃ | ||
| 脆化温度 | ASTM D-746 | -67.8 | ℃ | ||
| 玻璃转化温度 | ASTM E1356 | -26.1 | ℃ | ||
| ISO 11357-2 2 | -26 | ℃ | |||
| 维卡软化温度 | ASTM D-1525 | 168 | ℃ | ||
| 50°C/h, B (50N) | ISO 306 2 | 168 | ℃ | ||
| 线形膨胀系数 - 流动 | ASTM D-696 | 0.00013 | cm/cm/℃ | ||
| ISO 11359-2 2 | 0.00017 | cm/cm/℃ | |||
| 可燃性 | UL 阻燃等级 | 1.50 mm, NC, BK | UL 94 | HB | |
| 3.00 mm, NC, BK | UL 94 | HB | |||
| 燃烧性能 正常厚度 1.6mm | 1.50 mm, UL | ISO 1210 2 | HB | ||