BASFUltrason S 6010 PSU
Polymer,Thermoplastic,Polysulfone (PSU)
BASF
产品说明:
Ultrason S 6010 is an unreinforced, high molecular weightinjection-molding and extrusion grade with excellent chemicalresistance (stress crack resistance) and good solubility in typicalsolvents (N-Methylpyrrolidone, Dimethylacetamide, Dichlormethane)used e.g. in the production of membranes or coatings, with reducedoligomer content. It conforms to FDA re of 21 CFR177.1655.
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Transmission, Visible | 87 % @Thickness 2.00 mm | 87 % @Thickness 0.0787 in | ASTM D 1003 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 330 - 390 °C | 626 - 734 °F | |
| 模具温度 | 120 - 160 °C | 248 - 320 °F |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | Natural | |
| 商业地位 | North America and Europe | |
| FDA | 21 CFR 177.1655 | |
| Impact Modified | No | |
| NSF Std. 61 | Yes | |
| Primary Processing Technique | Injection Molding and Extrusion |
| 密度 | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| 吸水率 | 0.80 % | 0.80 % | ISO 62 |
| 平衡吸湿 | 0.30 % | 0.30 % | 23°C/50% R.H.; ISO 62 |
| 粘度测试 | 81 cm³/g | 81 cm³/g | Viscosity number |
| 线性成型收缩率,Flow | 0.0072 cm/cm | 0.0072 in/in | ISO 294 |
| 线性成型收缩率，横向 | 0.0077 cm/cm | 0.0077 in/in | ISO 294 |
| 熔体流动速率 | 30 g/10 min @Load 10.0 kg, Temperature 360 °C | 30 g/10 min @Load 22.0 lb, Temperature 680 °F | ISO 1133 |