高粘度PC 1804德国拜耳阻燃PC物性用途
PC 1804,1804德国拜耳,高粘度PC,阻燃PC
Makrolon® 1804
聚碳酸酯
Bayer MaterialScience - Polycarbonates
产品说明
MVR (300 °C/1.2 kg) 6.0 cm³/10 min; Extrusion; flame retardant; UL94V-2/1.5 mm and 3.0 mm; high viscosity; UV stabilized; optimizedfor low
plate-out; available in transparent, translucent and opaque colors;solid sheet
添加剂• 紫外线稳定剂• 阻燃
性能特点• 粘度，高• 阻燃性能
用途• 片材
RoHS 合规性• RoHS 合规
外观• 半透明• 不透明• 清晰/透明
加工方法• 挤出
UL 阻燃等级UL 94
1.50 mm V-2
6.00 mm V-0
灼热丝易燃指数IEC 60695-2-12
0.750 mm 850 °C
1.50 mm 875 °C
3.00 mm 960 °C
极限氧指数 12 31 % ISO 4589-2
Application of Flame from Small Burner 13 DIN 53438-1, -3
2.00 mm K1, F1
Burning Rate 14 (> 1.00 mm) Passed ISO 3795
Flash Ignition Temperature 480 °C ASTM D1929
Needle Flame Test IEC 60695-11-5
Method F: 1.50 mm 2.0 min
Method F: 2.00 mm 2.0 min
Method F: 3.00 mm 2.0 min
Method K: 1.50 mm 0.2 min
Method K: 2.00 mm 0.3 min
Method K: 3.00 mm 0.5 min
Self Ingnition Temperature 550 °C ASTM D1929