Makrolon® 2600
聚碳酸酯
Bayer MaterialScience - Polycarbonates ides.com/prospector
电气性能额定值单位制测试方法
耗散因数IEC 60250
23°C, 100 Hz 0.00050
23°C, 1 MHz 0.0090
漏电起痕指数IEC 60112
解决方案A 250 V
解决方案B 125 V
可燃性额定值单位制测试方法
UL 阻燃等级UL 94
2.50 mm HB
0.750 mm V-2
灼热丝易燃指数IEC 60695-2-12
1.00 mm 850 °C
1.50 mm 850 °C
2.00 mm 850 °C
3.00 mm 930 °C
4.00 mm 960 °C
热灯丝点火温度IEC 60695-2-13
1.00 mm 875 °C
1.50 mm 875 °C
2.00 mm 875 °C
3.00 mm 875 °C
4.00 mm 875 °C
极限氧指数 12 27 % ISO 4589-2
Application of Flame from Small Burner 13 DIN 53438-1, -3
2.00 mm K1, F1
Burning Rate 14 (> 1.00 mm) Passed ISO 3795
Flash Ignition Temperature 480 °C ASTM D1929
Needle Flame Test IEC 60695-11-5
Method F: 1.50 mm 1.0 min
Method F: 2.00 mm 1.0 min
Method F: 3.00 mm 2.0 min
Method K: 1.50 mm 0.1 min
Method K: 2.00 mm 0.1 min
Method K: 3.00 mm 0.2 min
Self Ingnition Temperature 550 °C ASTM D1929
光学性能额定值单位制测试方法
折射率 15 1.586 ISO 489
透射率ISO 13468-2
1000 μm 89.0 %
2000 μm 89.0 %
3000 μm 88.0 %
4000 μm 87.0 %
雾度(3000 μm) < 0.80 % ISO 14782
补充信息额定值单位制测试方法
Electrolytical Corrosion A1 IEC 60426
ISO Shortname PC,M,(,,)-18-9 ISO 7391
注射额定值单位制
加工（熔体）温度280 到320 °C