SABIC Innovative Plastics Lexan® LUX7430C PCCOPOLYMER
Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Lexan* LUX7430C Polycarbonate (PC) resin is anon-filled, injection moldable grade. This non-chlorinated,non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm/ 5VA rating at 3.0mm and is UV stabilized(F1 rating) providingadditional weathering capability. Lexan* LUX7430C is available inclear transparent and tinted color options that is an excellentcandidate for a wide variety of applications.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| 密度 | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 水分吸收 | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.13 % | 0.13 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0055 - 0.0075 cm/cm @Thickness 3.20 mm | 0.0055 - 0.0075 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 10 g/10 min @Load 1.20 kg, Temperature 300 °C | 10 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 化合物熔体指数 | 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 9.0 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 53.0 MPa | 7690 psi | 50 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 66.0 MPa | 9570 psi | 50 mm/min; ISO 527 |
| 67.0 MPa | 9720 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 55 % | 55 % | Type I, 50 mm/min; ASTM D638 |
| 56 % | 56 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
| 2.52 GPa | 365 ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | 101 MPa | 14600 psi | 2 mm/min; ISO 178 |
| 107 MPa | 15500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 2.45 GPa | 355 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.45 GPa | 355 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| 0.810 J/cm @Temperature -30.0 °C | 1.52 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 悬壁梁无缺口冲击强度 | NB | NB | ASTM D4812 |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ASTM D4812 | |
| 悬壁梁缺口冲击强度 | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*3; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| 简支梁无缺口冲击强度 | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 1.00 J/cm² | 4.76 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 落锤总能量 | 64.0 J @Temperature 23.0 °C | 47.2 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电常数 | 2.79 @Frequency 1.00e+9 Hz | 2.79 @Frequency 1.00e+9 Hz | ASTM ES 7-83 |
| 耗散因数 | 0.0057 @Frequency 1.10e+9 Hz | 0.0057 @Frequency 1.10e+9 Hz | ASTM ES 7-83 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 37.2 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 77.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 42.8 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 37.2 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 79.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 43.9 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 载荷下热变形温度(0.46 MPa) | 131 °C | 268 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 131 °C @Thickness 3.20 mm | 268 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 120 °C @Thickness 3.20 mm | 248 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 136 °C | 277 °F | Rate B/50; ASTM D1525 |
| 137 °C | 279 °F | Rate B/50; ISO 306 | |
| 139 °C | 282 °F | Rate B/120; ISO 306 | |
| UL RTI | 125 °C | 257 °F | UL 746B |
| UL RTI，机械冲击 | 120 °C | 248 °F | UL 746B |
| UL RTI，机械无冲击 | 125 °C | 257 °F | UL 746B |
| 可燃性(UL94) | V-2 @Thickness 0.400 mm | V-2 @Thickness 0.0157 in | UL 94 |
| V-1 @Thickness 1.00 mm | V-1 @Thickness 0.0394 in | UL 94 | |
| V-0 @Thickness 1.20 mm | V-0 @Thickness 0.0472 in | UL 94 | |
| 5VA @Thickness 3.00 mm | 5VA @Thickness 0.118 in | UL 94 | |
| 灼热丝试验 | 850 °C | 1560 °F | IEC 60695-2-13 |
| 960 °C @Thickness 1.20 mm | 1760 °F @Thickness 0.0472 in | IEC 60695-2-12 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Transmission, Visible | >= 91 % | >= 91 % | 2.54 mm; ASTM D1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 球压试验，125°C+/-2℃ | Pass | IEC 60695-10-2 |
| UV-light, water exposure/immersion | F1 | UL 746C |
我司销售以下原料:
<<< PC 30D G/10-V0 意大利拉题 ## 用途： 其它 特性备注：LowOptical Density 尺寸稳定性良好 卤化 无锑 烟释放，低 重要参数： 密度:1.26 g/cm3 成型收缩率:0.45% 维卡软化点:145 ℃ 热变形温度:140 ℃ 生产厂商：意大利拉题公司
<<< PC M7027B 泰国三菱 ## 用途： 其它 重要参数： 熔体流动速率:2.8g/10min 密度:1.2 g/cm3 拉伸强度:50 MPa 弯曲强度:98 MPa 弯曲模量:2500 MPa热变形温度:128 ℃ 生产厂商：泰国三菱化学有限公司
<<< PC EGN2020KR 三菱工程塑料 ## 用途： 纤维 重要参数： 密度:1.35g/cm3 吸水率:0.11 % 成型收缩率:0.15 % 缺口冲击强度:7 拉伸强度:90 MPa 断裂伸长率:2.9 %弯曲强度:139 MPa 弯曲模量:5500 MPa 热变形温度:137 ℃生产厂商：日本三菱工程塑料株式会社
<<< PC 701-10 美国Trinseo ## 用途： 其它特性备注：特点：既有透明度，也具有增强的阻燃性能。 重要参数： 熔体流动速率:10 g/10min 密度:1.2 g/cm3吸水率:0.23 % 成型收缩率:0.5 % 缺口冲击强度:30 拉伸强度:60 MPa 断裂伸长率:50 % 弯曲强度:100MPa 弯曲模量:2400 MPa 维卡软化点:149 ℃ 热变形温度:123 ℃生产厂商：美国Trinseo公司