Plastcom SLOVAMID 66 BT TS PA66, basic type, thermalstability
Nylon 66, Heat Stabilized
Plastcom spol. s r.o.
产品说明：
Features
Modified for general use, with excellent manufacturingproperties, characterized by high strength and toughness also atminus temperatures. Used in automotive, electrical, engineering andconsumer goods industry. Application: electric tools, gear wheels,clamps, fasteners, toolbodies, webbing slings for cableharnesses.
Packaging, transport, stocking
The product is packed in hermetically closedthick-walled 25 kg PE bags, on a 1.000 kg palette coated in astretch foil, in big bags with a thick PE foil fixed on a 1.000 kgpalette, in paper octabins with a thick PE foil fixed on a 1.000 kgpalette or in other packaging according to customer re transport is provided in closed-up vehicles where the materialis protected against movement and mechanical damage. The productrequires stocking in closed-up, dry places protected against sunand thermal radiation.
Information Provided by Plastcom spol. sr.o.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.13 g/cc | 0.0408 lb/in³ | |
| 粘度测量 | 1.8 - 1.93 | 1.8 - 1.93 | |
| 线性成型收缩率 | 0.018 cm/cm | 0.018 in/in | |
| 线性成型收缩率，横向 | 0.0193 cm/cm | 0.0193 in/in | |
| 熔体流动速率 | 4.0 g/10 min @Load 0.325 kg, Temperature 270 °C | 4.0 g/10 min @Load 0.716 lb, Temperature 518 °F |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 80.0 MPa | 11600 psi | |
| 伸长率 (断裂) | 3.0 % | 3.0 % | |
| 拉伸模量 | 3.20 GPa | 464 ksi | |
| 弯曲强度 | 100 MPa | 14500 psi | |
| 弯曲模量 | 2.70 GPa | 392 ksi | |
| 简支梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | |
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ||
| 简支梁缺口冲击强度 | 0.200 J/cm² @Temperature -20.0 °C | 0.952 ft-lb/in² @Temperature -4.00 °F | |
| 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| 表面电阻 | 1.00e+14 ohm | 1.00e+14 ohm | |
| 介电强度 | 30.0 kV/mm | 762 kV/in | |
| 相比耐漏电起痕指数(CTI) | 600 V | 600 V |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | 260 °C | 500 °F | |
| 载荷下热变形温度(1.8 MPa) | 68.0 °C | 154 °F | |
| 维卡软化温度 | 250 °C | 482 °F | B |
| 可燃性(UL94) | HB | HB | |
| 灼热丝试验 | 960 °C | 1760 °F |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 280 - 300 °C | 536 - 572 °F | |
| 模具温度 | 80.0 - 90.0 °C | 176 - 194 °F | |
| 干燥温度 | 80.0 °C | 176 °F | |
| 干燥时间 | 4 hour | 4 hour | |
| 水分含量 | 0.15 % | 0.15 % | |
| 注射压力 | 70.0 - 120 MPa | 10200 - 17400 psi |