TOPAS®6013M-07
Cyclic Olefin Copolymer
Topas Advanced Polymers, Inc.
产品说明:
Product Description
TOPAS 6013M-07 is an injection molding grade with a wide processingwindow, especially suited for blow molding processes including IBMand ISBM. It is a glass-clear amorphous polymer with outstandingmoisture barrier, chemical resistance, high purity and anon-reactive surface making it an excellent choice for healthcareand other high-tech products. Lower leachables and extractables ofTOPAS COC preserve content stability and quality. It is a non-polarsubstrate that does not promote adsorption, denaturation,aggregation, or precipitation like glass can. This grade has a high(130°C) heat distortion temperature to withstand 121°C steamsterilization protocols, as well as gamma and EtO procedures.
Selected Applications
Drug delivery
Prefilled syringes, vials, cartridges
Bottles and tubes
Surgical instruments
IV containers and components
Labware
Optics
Electronics
Food packaging
Healthcare and food contact
Leading Attributes
Low leachables & extractables, low water transmission
Non-ionic, does not promote adsorption like glass
Minimally reactive
Chemically resistant to alcohol, acetone, and acrylates
Transparent, withstands EtO/gamma/steam sterilization
Temperature resistance, clarity and purity
Clarity, low birefringence, low moisture sensitivity
Low dielectric constant, thermoplastic
Not manufactured with BPA, phthalates, or halogens
Broad regulatory compliance
Related Grades for Injection Molding, Healthcare, Optics andDiagnostics
TOPAS 6013S-04 - standard processing version with standardflow
TOPAS 6015S-04 - higher heat distortion temperature (150°C) for134°C protocols
TOPAS 6017S-04 - our most heat distortion resistant IM grade(HDT=170°C)
TOPAS 5013L-10 - high flow grade; lubricated version for greaterprocessing versatility
TOPAS 5013S-04 - high flow grade without lubricant
TOPAS IT X1 - impact grade for applications requiring extratoughness
物性信息:
基本信息 | |
---|---|
特性 |
|
用途 |
|
机构评级 |
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.02 | g/cm³ | ISO 1183 |
熔流率(熔体流动速率) (260°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
溶化体积流率(MVR) (260°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
收缩率 1 | 0.50 到 0.70 | % | 内部方法 |
吸水率 (饱和, 23°C) | 0.010 | % | ISO 62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 2900 | MPa | ISO 527-2/1A/1 |
拉伸应力 (屈服) | 63.0 | MPa | ISO 527-2/1A/50 |
拉伸应变 (屈服) | 2.6 | % | ISO 527-2/1A/50 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 (23°C) | 14 | kJ/m² | ISO 179/1eU |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
热变形温度 (0.45 MPa, 未退火) | 130 | °C | ISO 75-2/B |
玻璃转化温度 | 142 | °C | ISO 11357-2 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
折射率 | 1.530 | ISO 489 | |
透射率 | 91.0 | % | ISO 13468-2 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
料筒后部温度 | 230 到 260 | °C | |
料筒中部温度 | 240 到 270 | °C | |
料筒前部温度 | 250 到 280 | °C | |
射嘴温度 | 240 到 300 | °C | |
加工(熔体)温度 | 240 到 300 | °C | |
模具温度 | 95.0 到 125 | °C | |
注塑压力 | 50.0 到 110 | MPa | |
注射速度 | 中等偏快 | ||
保压 | 30.0 到 60.0 | MPa | |
背压 | < 15.0 | MPa | |
Screw Speed | 50 到 200 | rpm |
注射说明 |
---|
Feed Temperature: <100°C (<212°F)Max. Residence Time: <15minutes; short interruption to cycle, reduce Tx = 170°C(338°F)Injection Speed: 50 - 150 mm/sec (2.0 - 6.0 in/sec)NozzleType: Free Flow |
备注 | |
---|---|
1 . | Dependent on process conditions and part design. |