TOPAS®5013L-10
Cyclic Olefin Copolymer
Topas Advanced Polymers, Inc.
产品说明：
Product Description
TOPAS 5013L-10 is a high flow, internally lubricated injectionmolding grade with a 130°C heat distortion temperature. It is aglass-clear amorphous polymer with outstanding moisture barrier,chemical resistance, high purity and a non-reactive surface makingit an excellent choice for healthcare and other high-tech products.The 5013 resin series features high flow characteristics forexcellent mold detail replication. This grade has a high heatdistortion temperature to withstand 95°C PCR protocols, is suitablefor gamma or EtO procedures.
Selected Applications
Labware
Microplates and biochips
Microfluidics
Optics
Electronics
Cuvettes
Healthcare
Leading Attributes
Temperature resistant with glass-like clarity;purity
Heat and chemical resistant, clarity andpurity
Exceptional mold detail replication;machinable
Clarity, low birefringence, low moisturesensitivity
Low dielectric constant, high flow,thermoplastic
More UV transparent than most resins (see8007X10)
Broad regulatory compliance
Related Grades for Injection Molding, Healthcare, Opticsand Diagnostics
TOPAS 5013S-04 - non-lubricated high flowversion
TOPAS 6013S-04 - general purpose version with standardflow
TOPAS 6013M-07 - broader processing version especiallysuited for IBM/ISBM
TOPAS 6015S-04 - higher heat distortion temperature(150°C) for 134°C protocols
TOPAS IT X1 - impact grade for applications requiringextra toughness
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (260°C/2.16 kg) | 44 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） (260°C/2.16 kg) | 48.0 | cm³/10min | ISO 1133 |
| 收缩率 1 | 0.10 到 0.30 | % | 内部方法 |
| 吸水率 (饱和, 23°C) | 0.010 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 3200 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 46.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 1.7 | % | ISO 527-2/1A/50 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 (23°C) | 1.6 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 (23°C) | 13 | kJ/m² | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 (0.45 MPa, 未退火) | 127 | °C | ISO 75-2/B |
| 玻璃转化温度 | 134 | °C | ISO 11357-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | > 1.0E+16 | ohms·cm | IEC 60093 |
| 相对电容率 | IEC 60250 | ||
| 1 kHz | 2.35 | IEC 60250 | |
| 10 kHz | 2.35 | IEC 60250 | |
| 漏电起痕指数 | > 600 | V | IEC 60112 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 折射率 | 1.533 | ISO 489 | |
| 透射率 | 91.0 | % | ISO 13468-2 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 100 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 料筒后部温度 | 230 到 260 | °C | |
| 料筒中部温度 | 240 到 280 | °C | |
| 料筒前部温度 | 260 到 290 | °C | |
| 射嘴温度 | 240 到 300 | °C | |
| 加工（熔体）温度 | 240 到 300 | °C | |
| 模具温度 | 95.0 到 125 | °C | |
| 注塑压力 | 50.0 到 110 | MPa | |
| 注射速度 | 中等偏快 | ||
| 保压 | 30.0 到 60.0 | MPa | |
| 背压 | < 15.2 | MPa | |
| 螺杆转速 | 50 到 200 | rpm |
| 注射说明 |
|---|
| Feed Temperature: <100°C (<212°F)Max. Residence TIme:<15 min; short interruptions to cycle >10 minutes: reduceTx=170°C (338°F)Injection Speed: 50 to 150 mm/sec (2.0 - 6.0in/sec)Nozzle type: Free flow |
| 备注 | |
|---|---|
| 1 . | Dependent on processing conditions and partdesign. |
简介：
TOPAS®是TOPAS ADVANCED POLYMERSGmbH公司开发出来的环烯烃类共聚物（COC）的商品名，是具有环状烯烃结构的非晶性透明共聚高分子。
TOPAS®具有与PMMA（聚甲基丙烯酸甲酯、丙烯酸树脂）相匹敌的光学性能以及具有高于PC（聚碳酸酯）的耐热性，还由于低吸水性而具有比PMMA和PC更加优良的尺寸稳定性等，在市场上获得了很高的评价。再有，TOPAS®还具有改善水蒸汽气密性，增加刚性、耐热性，能赋予易切割性等优点，作为适合于用作传统材料的改性用材料，它在包装材料领域里的开发活动正在推进之中。
特点：
优良的光学性能
TOPAS®具有能与PMMA相匹敌的光学性能和与PC同等或超过它的耐热性，还由于它几乎不吸水，因而还是具有高度的尺寸稳定性等优良的性能的树脂，它在光学市场领域获得了很高的评价。
优良的光学性能 | Unit | TOPAS®5013 | PC | PMMA |
全光线透过率* | % | 91 | 87-89 | 91-92 |
折射率 | - | 1.53 | 1.59 | 1.49 |
阿贝数 | - | 58 | 30 - 31 | 57 - 58 |
双折射 | nm | < 20 | < 65 | < 20 |
光弹性系数 | 10-12Pa-1 | -2 to -7 | 66 to 70 | -4.5 to -4.8 |
饱和吸水率 | % | 0.01 | 0.2 | 0.3 |
*实验方法：ISO 13468-1
水蒸汽气密性
TOPAS®具有非常高的水蒸汽气密性，它在医疗、包装材料领域里的应用正在开发。
安全性
TOPAS®的安全性也非常优良，它的基本品级已经在美国FDA、美国医药局ClassVI上登记注册。在医疗·检测仪器领域的应用受到广泛的关注。
电性能
TOPAS®在高频领域显示出优良的电性能，可望在天线等的电子器件用途方面扩展市场。
主要用途：
COC: TOPAS®被用于 LED阀套
COC树脂"TOPAS®"被用于水质检测瓶
开发出含有 TOPAS®的缓冲材料
TOPAS®薄型导光板实现了Zui高等级的薄壁流动性