电气绝缘件PPO 沙伯基础PPOV01525 低翘曲PPO 性能沙特基础NORYL™PPE+PSV01525
>(PPE+PS)-MGF15-FR< 阻燃等级: V-1• V-0 • 5VA 比重: 1.13 g/cm³ 缺口冲击: 5.10 kJ/m² 符合规定: UL材料特性: 尺寸稳定 •低翘曲材料用途: 电器内部构件 •电气外壳面板 • 电气绝缘件 • 外壳
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| 介电常数 | 2.9 @Frequency 1.00e+6 Hz | 2.9 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.0 @Frequency 50.0 - 60.0 Hz | 3.0 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| 介电强度 | 16.0 kV/mm @Thickness 3.20 mm | 406 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
| 26.0 kV/mm @Thickness 1.60 mm | 660 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |
| 33.0 kV/mm @Thickness 0.800 mm | 838 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |
| 耗散因数 | 0.0030 @Frequency 1.00e+6 Hz | 0.0030 @Frequency 1.00e+6 Hz | IEC 60250 |
| 0.0060 @Frequency 50.0 - 60.0 Hz | 0.0060 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 175 V | 175 V | IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 50.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 27.8 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 66.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 36.7 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| 线性热膨胀系数,横向流动 | 52.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 28.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 33.3 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 导热系数 | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 125 °C | <= 257 °F | IEC 60695-10-2 |
| 载荷下热变形温度(1.8 MPa) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 120 °C @Thickness 3.20 mm | 248 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 130 °C | 266 °F | Rate B/50; ISO 306 |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| 140 °C | 284 °F | Rate B/50; ASTM D1525 | |
| 140 °C | 284 °F | Rate A/50; ISO 306 | |
| UL RTI | 50.0 °C | 122 °F | UL 746B |
| UL RTI，机械冲击 | 50.0 °C | 122 °F | UL 746B |
| UL RTI，机械无冲击 | 50.0 °C | 122 °F | UL 746B |
| 可燃性(UL94) | V-1 @Thickness 1.20 mm | V-1 @Thickness 0.0472 in | UL 94 |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 | |
| 5VA @Thickness 3.00 mm | 5VA @Thickness 0.118 in | UL 94 | |
| 极限氧指数 | 32 % | 32 % | ISO 4589 |
| 灼热丝试验 | 960 °C @Thickness 3.20 mm | 1760 °F @Thickness 0.126 in | IEC 60695-2-12 |