NORYL™PPE+PS EM6101 汽车内部件PPO沙伯基础PPOEM6101
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| 吸水率 | 0.20 % @Time 86400 sec | 0.20 % @Time 24.0 hour | ASTM D570 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 50 % | 50 % | Type I, 50 mm/min; ASTM D638 |
| 弯曲强度 | 81.0 MPa | 11700 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 弯曲模量 | 2.30 GPa | 334 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 3.20 J/cm | 5.99 ft-lb/in | ASTM D256 |
| 1.60 J/cm @Temperature -40.0 °C | 3.00 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| 落锤总能量 | 53.0 J | 39.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 25.0 J @Temperature -30.0 °C | 18.4 ft-lb @Temperature -22.0 °F | Instrumented Impact Energy @ peak; ASTM D3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 93.6 µm/m-°C @Temperature 0.000 - 100 °C | 52.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM E 831 |
| 载荷下热变形温度(0.46 MPa) | 123 °C @Thickness 6.40 mm | 253 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 121 °C @Thickness 6.40 mm | 250 °F @Thickness 0.252 in | unannealed; ASTM D648 |