直营杜邦PA66 11C40

DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66(Unverified Data**) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.47 g/cc0.0531 lb/in³DAM; ISO 1183吸水率6.0%

@Thickness 2.00 mm

6.0 %

@Thickness 0.0787 in

DAM; Sim. to ISO 62水分吸收1.60 %

@Thickness 2.00 mm

1.60 %

@Thickness 0.0787 in

DAM; Sim. to ISO 62饱和吸水率1.1 %1.1 %DAM; Immersion 24h; ASTMD570线性成型收缩率,Flow0.0090 cm/cm0.0090 in/inDAM; ISO 294-42577线性成型收缩率，横向0.0090 cm/cm0.0090 in/inDAM; ISO 294-4 2577机械性能额定值(公制)额定值 (英制)测试方法抗张强度(断裂)63.0 MPa9140 psi50%RH; ISO 527-1/-2
90.0 MPa13100 psiDAM; ISO 527-1/-2抗张强度3.93 MPa

@Strain 0.500 %, Temperature 150 °C

570 psi

@Strain 0.500 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
6.20 MPa

@Strain 0.700 %, Temperature 150 °C

899 psi

@Strain 0.700 %, Temperature 302 °F

DAM; ISO 11403-1 -2
10.38 MPa

@Strain 1.70 %, Temperature 150 °C

1505 psi

@Strain 1.70 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
11.76 MPa

@Strain 0.500 %, Temperature 23.0 °C

1706 psi

@Strain 0.500 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
16.06 MPa

@Strain 3.50 %, Temperature 150 °C

2329 psi

@Strain 3.50 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
17.0 MPa

@Strain 2.70 %, Temperature 150 °C

2470 psi

@Strain 2.70 %, Temperature 302 °F

DAM; ISO 11403-1 -2
19.0 MPa

@Strain 5.00 %, Temperature 150 °C

2760 psi

@Strain 5.00 %, Temperature 302 °F

50%RH; ISO 11403-1 -2
19.43 MPa

@Strain 0.300 %, Temperature -40.0 °C

2818 psi

@Strain 0.300 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
20.27 MPa

@Strain 1.00 %, Temperature 23.0 °C

2940 psi

@Strain 1.00 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
24.6 MPa

@Strain 6.00 %, Temperature 150 °C

3570 psi

@Strain 6.00 %, Temperature 302 °F

DAM; ISO 11403-1 -2
27.27 MPa

@Strain 0.500 %, Temperature 0.000 °C

3955 psi

@Strain 0.500 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
29.7 MPa

@Strain 13.0 %, Temperature 150 °C

4310 psi

@Strain 13.0 %, Temperature 302 °F

DAM; ISO 11403-1 -2
30.03 MPa

@Strain 1.90 %, Temperature 23.0 °C

4355 psi

@Strain 1.90 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
30.3 MPa

@Strain 0.500 %, Temperature 0.000 °C

4390 psi

@Strain 0.500 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
33.3 MPa

@Strain 0.600 %, Temperature 23.0 °C

4830 psi

@Strain 0.600 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
36.3 MPa

@Strain 0.500 %, Temperature -40.0 °C

5260 psi

@Strain 0.500 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
42.11 MPa

@Strain 3.90 %, Temperature 23.0 °C

6108 psi

@Strain 3.90 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
56.33 MPa

@Strain 0.900 %, Temperature -40.0 °C

8170 psi

@Strain 0.900 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
58.6 MPa

@Strain 1.10 %, Temperature 23.0 °C

8500 psi

@Strain 1.10 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
61.78 MPa

@Strain 1.20 %, Temperature 0.000 °C

8960 psi

@Strain 1.20 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
63.9 MPa

@Strain 1.10 %, Temperature 0.000 °C

9270 psi

@Strain 1.10 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
64.161 MPa

@Strain 35.0 %, Temperature 23.0 °C

9305.8 psi

@Strain 35.0 %, Temperature 73.4 °F

50%RH; ISO 11403-1 -2
66.1 MPa

@Strain 1.00 %, Temperature -40.0 °C

9590 psi

@Strain 1.00 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
70.7 MPa

@Strain 1.40 %, Temperature 23.0 °C

10300 psi

@Strain 1.40 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
76.3 MPa

@Strain 1.60 %, Temperature 0.000 °C

11100 psi

@Strain 1.60 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
78.05 MPa

@Strain 1.30 %, Temperature -40.0 °C

11320 psi

@Strain 1.30 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
79.8 MPa

@Strain 1.30 %, Temperature -40.0 °C

11600 psi

@Strain 1.30 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
80.8 MPa

@Strain 1.80 %, Temperature 23.0 °C

11700 psi

@Strain 1.80 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
81.1 MPa

@Strain 1.50 %, Temperature 0.000 °C

11800 psi

@Strain 1.50 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
84.38 MPa

@Strain 1.90 %, Temperature 0.000 °C

12240 psi

@Strain 1.90 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2
90.91 MPa

@Strain 3.70 %, Temperature 23.0 °C

13190 psi

@Strain 3.70 %, Temperature 73.4 °F

DAM; ISO 11403-1 -2
93.5 MPa

@Strain 1.70 %, Temperature -40.0 °C

13600 psi

@Strain 1.70 %, Temperature -40.0 °F

50%RH; ISO 11403-1 -2
93.7 MPa

@Strain 1.90 %, Temperature 0.000 °C

13600 psi

@Strain 1.90 %, Temperature 32.0 °F

DAM; ISO 11403-1 -2
96.12 MPa

@Strain 1.70 %, Temperature -40.0 °C

13940 psi

@Strain 1.70 %, Temperature -40.0 °F

DAM; ISO 11403-1 -2
99.88 MPa

@Strain 4.40 %, Temperature 0.000 °C

14490 psi

@Strain 4.40 %, Temperature 32.0 °F

50%RH; ISO 11403-1 -2