DuPont Performance Polymers Zytel® 135F NC010 Nylon 66(Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.01 g/cc | 0.0365 lb/in³ | |
| 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | |
| 吸水率 | 8.5 % @Thickness 2.00 mm | 8.5 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | 2.70 % @Thickness 2.00 mm | 2.70 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 粘度 | 64000 cP @Shear Rate 5000 1/s, Temperature 315 °C | 64000 cP @Shear Rate 5000 1/s, Temperature 599 °F | ISO 11403-1 -2 |
| 83000 cP @Shear Rate 5000 1/s, Temperature 295 °C | 83000 cP @Shear Rate 5000 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
| 105000 cP @Shear Rate 5000 1/s, Temperature 275 °C | 105000 cP @Shear Rate 5000 1/s, Temperature 527 °F | ISO 11403-1 -2 | |
| 134000 cP @Shear Rate 500 1/s, Temperature 315 °C | 134000 cP @Shear Rate 500 1/s, Temperature 599 °F | ISO 11403-1 -2 | |
| 195000 cP @Shear Rate 500 1/s, Temperature 295 °C | 195000 cP @Shear Rate 500 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
| 284000 cP @Shear Rate 500 1/s, Temperature 275 °C | 284000 cP @Shear Rate 500 1/s, Temperature 527 °F | ISO 11403-1 -2 | |
| 粘度测试 | 150 cm³/g | 150 cm³/g | DAM; ISO 307 1157 1628 |
| 线性成型收缩率,Flow | 0.0070 cm/cm | 0.0070 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 64 | 64 | 50%RH; ISO 2039-2 |
| 87 | 87 | DAM; ISO 2039-2 | |
| 洛氏硬度（R 级） | 116 | 116 | 50%RH; ISO 2039-2 |
| 123 | 123 | DAM; ISO 2039-2 |