PA66 70G30HSL杜邦尼龙深圳直营
| 密度 | 1.37 g/cc | 0.0495 lb/in³ | DAM; ISO 1183 |
| 吸水率 | 6.0 % @Thickness 2.00 mm | 6.0 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | 1.90 % @Thickness 2.00 mm | 1.90 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 粘度 | 46970 cP @Shear Rate 5000 1/s, Temperature 305 °C | 46970 cP @Shear Rate 5000 1/s, Temperature 581 °F | ISO 11403-1 -2 |
| 58620 cP @Shear Rate 5000 1/s, Temperature 295 °C | 58620 cP @Shear Rate 5000 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
| 74567 cP @Shear Rate 5000 1/s, Temperature 285 °C | 74567 cP @Shear Rate 5000 1/s, Temperature 545 °F | ISO 11403-1 -2 | |
| 119700 cP @Shear Rate 500 1/s, Temperature 305 °C | 119700 cP @Shear Rate 500 1/s, Temperature 581 °F | ISO 11403-1 -2 | |
| 154240 cP @Shear Rate 500 1/s, Temperature 295 °C | 154240 cP @Shear Rate 500 1/s, Temperature 563 °F | ISO 11403-1 -2 | |
| 201130 cP @Shear Rate 500 1/s, Temperature 285 °C | 201130 cP @Shear Rate 500 1/s, Temperature 545 °F | ISO 11403-1 -2 | |
| 线性成型收缩率,Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.011 cm/cm | 0.011 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 88 | 88 | 50%RH; ISO 2039-2 |
| 104 | 104 | DAM; ISO 2039-2 | |
| 洛氏硬度（R 级） | 117 | 117 | 50%RH; ISO 2039-2 |
| 124 | 124 | DAM; ISO 2039-2 | |
| 抗张强度(断裂) | 130 MPa | 18900 psi | 50%RH; ISO 527-1/-2 |
| 200 MPa | 29000 psi | DAM; ISO 527-1/-2 | |
| 伸长率 (断裂) | 3.4 % | 3.4 % | DAM; ISO 527-1/-2 |
| 5.0 % | 5.0 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 7.00 GPa | 1020 ksi | 50%RH; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | DAM; ISO 527-1/-2 |