Zytel® 70G20HSL NC010 Nylon 66 物性表
物理性能额定值 (公制)额定值 (英制)测试方法密度1.29 g/cc0.0466 lb/in³DAM; ISO 1183WaterAbsorption2.1 %@Temperature 23.0 °C
2.1 %@Temperature 73.4 °F
E 50%RH; DAM; ISO 62, Similar to6.8 %
@Temperature 23.0 °C
6.8 %@Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to线性成型收缩率,Flow0.0040cm/cm@Thickness 2.00 mm
0.0040 in/in@Thickness 0.0787 in
DAM; ISO 294-4线性成型收缩率,横向0.012 cm/cm@Thickness 2.00 mm
0.012 in/in@Thickness 0.0787 in
DAM; ISO 294-4机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度(M 级)858550%RH; ISO2039/2102102DAM; ISO 2039/2洛氏硬度(R 级)11511550%RH; ISO 2039/2
122122DAM; ISO 2039/2抗张强度(断裂)103 MPa
@Temperature 23.0 °C
14900 psi@Temperature 73.4 °F
50%RH; ISO 527159 MPa
@Temperature 23.0 °C
23100 psi@Temperature 73.4 °F
DAM; ISO 527抗张强度17.5 MPa@Strain 0.530 %, Temperature 120 °C
2540 psi@Strain 0.530 %, Temperature 248 °F
50%RH; ISO 52718.5 MPa
@Strain 0.520 %, Temperature 90.0 °C
2680 psi@Strain 0.520 %, Temperature 194 °F
50%RH; ISO 52720.5 MPa
@Strain 0.520 %, Temperature 60.0 °C
2970 psi@Strain 0.520 %, Temperature 140 °F
50%RH; ISO 52722.2 MPa
@Strain 0.630 %, Temperature 120 °C
3220 psi@Strain 0.630 %, Temperature 248 °F
DAM; ISO 52723.0 MPa
@Strain 0.480 %, Temperature 40.0 °C
3340 psi@Strain 0.480 %, Temperature 104 °F
50%RH; ISO 52724.5 MPa
@Strain 0.610 %, Temperature 90.0 °C
3550 psi@Strain 0.610 %, Temperature 194 °F
DAM; ISO 52725.9 MPa
@Strain 0.440 %, Temperature 23.0 °C
3760 psi@Strain 0.440 %, Temperature 73.4 °F
50%RH; ISO 52726.2 MPa
@Strain 0.460 %, Temperature 60.0 °C
3800 psi@Strain 0.460 %, Temperature 140 °F
DAM; ISO 52727.7 MPa
@Strain 0.270 %, Temperature -20.0 °C
4020 psi@Strain 0.270 %, Temperature -4.00 °F
50%RH; ISO 52728.8 MPa
@Strain 0.330 %, Temperature 0.000 °C
4180 psi@Strain 0.330 %, Temperature 32.0 °F
50%RH; ISO 52730.6 MPa
@Strain 1.06 %, Temperature 120 °C
4440 psi@Strain 1.06 %, Temperature 248 °F
50%RH; ISO 52733.2 MPa
@Strain 0.360 %, Temperature 40.0 °C
4820 psi@Strain 0.360 %, Temperature 104 °F
DAM; ISO 52733.4 MPa
@Strain 1.04 %, Temperature 90.0 °C
4840 psi@Strain 1.04 %, Temperature 194 °F
50%RH; ISO 52735.9 MPa
@Strain 0.250 %, Temperature 23.0 °C
5210 psi@Strain 0.250 %, Temperature 73.4 °F
DAM; ISO 52737.4 MPa
@Strain 1.04 %, Temperature 60.0 °C
5420 psi@Strain 1.04 %, Temperature 140 °F
50%RH; ISO 52738.3 MPa
@Strain 1.26 %, Temperature 120 °C
5550 psi@Strain 1.26 %, Temperature 248 °F
DAM; ISO 52740.4 MPa
@Strain 1.59 %, Temperature 120 °C
5860 psi@Strain 1.59 %, Temperature 248 °F
50%RH; ISO 52741.2 MPa
@Strain 0.960 %, Temperature 40.0 °C
5980 psi@Strain 0.960 %, Temperature 104 °F
50%RH; ISO 52742.0 MPa
@Strain 1.22 %, Temperature 90.0 °C
6090 psi@Strain 1.22 %, Temperature 194 °F
DAM; ISO 52745.1 MPa
@Strain 1.56 %, Temperature 90.0 °C
6540 psi@Strain 1.56 %, Temperature 194 °F
50%RH; ISO 52745.4 MPa
@Strain 0.920 %, Temperature 60.0 °C
6580 psi@Strain 0.920 %, Temperature 140 °F
DAM; ISO 52746.8 MPa
@Strain 0.880 %, Temperature 23.0 °C
6790 psi@Strain 0.880 %, Temperature 73.4 °F
50%RH; ISO 527