产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.2 | 23/23℃ | |
| 熔体流动速率 | 200℃ 10kg | ASTM D-1238 | 34 | g/10min | |
| 机械性能 | IZOD冲击强度 | 1/8" | ASTM D-256 | 27 | kg.cm/cm |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 3.7 | ft.lb/in | |
| 引张强度 | ASTM D-638 | 430 | kg/cm2 | ||
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 15 | kg.cm/cm | |
| 弯曲弹性率 | ASTM D-790 | 3.2×105 | lb/in2 | ||
| 弯曲强度 | ASTM D-790 | 660 | kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 9370 | lb/in2 | ||
| 洛氏硬度 | ASTM D-785 | 102 | R | ||
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 2.8 | ft.lb/in | |
| 伸长率 | ASTM D-638 | 20 | % | ||
| 引张强度 | ASTM D-638 | 6100 | lb/in2 | ||
| 弯曲弹性率 | ASTM D-790 | 2.3×104 | kg/cm2 | ||
| 热性能 | 热变形温度 | ASTM D-648 | 96(205) | ℃ | |
| 热变形温度 | ASTM D-648 | 81(178) | ℉ | ||
| 维卡软化点 | ASTM D-1525 | 214 | ℉ | ||
| 燃烧性 | File No. E56070 UL&C-UL | 1/10"V-0，1/8"5VA | |||
| 维卡软化点 | ASTM D-1525 | 101 | ℃ | ||
塑料ABS树脂是产量大，应用广泛的聚合物，它将RB，PAN，PS的各种性能有机地统一起来，兼具韧，硬，刚相均衡的优良力学性能。ABS是丙烯腈、丁二烯和苯乙烯的三元共聚物，A代表丙烯腈，B代表丁二烯，S代表苯乙烯。经过实际使用发现：ABS塑料管材，不耐硫酸腐蚀，遇硫酸就粉碎性破裂。
由于具有三种组成，而赋予了其很好的性能；丙烯腈赋予ABS树脂的化学稳定性、耐油性、一定的刚度和硬度；丁二烯使其韧性、冲击性和耐寒性有所提高；苯乙烯使其具有良好的介电性能，并呈现良好的加工性。
大部分ABS是无毒的，不透水，但略透水蒸气，吸水率低，室温浸水一年吸水率不超过1%而物理性能不起变化。ABS树脂制品表面可以抛光，能得到高度光泽的制品。比一般塑料的强度高3-5倍。
ABS具有优良的综合物理和机械性能，较好的低温抗冲击性能。尺寸稳定性。电性能、耐磨性、抗化学药品性、染色性、成品加工和机械加工较好。ABS树脂耐水、无机盐、碱和酸类，不溶于大部分醇类和烃类溶剂，而容易溶于醛、酮、酯和某些氯代烃中。ABS树脂热变形温度低可燃，耐热性较差。熔融温度在217~237℃，热分解温度在250℃以上。如今的市场上改性ABS材料，很多都是掺杂了水口料再生料。导致客户成型产品性能不是很稳定。