TOPAS®6015S-04
Cyclic Olefin Copolymer
Topas Advanced Polymers, Inc.
产品说明：
Product Description
TOPAS 6015S-04 is a general purpose injection molding grade. It isa glass-clear amorphous polymer with outstanding moisture barrier,chemical resistance, high purity and a non-reactive surface makingit an excellent choice for optics, healthcare and other high-techproducts. Lower leachables and extractables of TOPAS COC preservefood and drug stability and quality. It is a non-polar substratethat does not promote adsorption, denaturation, aggregation, orprecipitation like glass can. This grade has a high (150°C) heatdistortion temperature to withstand 121°C and 134°C steam and dryheat sterilization protocols, as well as gamma and EtOprocedures.
Selected Applications
Drug delivery
Prefilled syringes, vials, cartridges
Bottles and tubes
Surgical instruments
IV containers and components
Labware
Optics
Electronics
Food packaging
Healthcare and food contact
Leading Attributes
Low leachables & extractables, low water transmission
Non-ionic, does not promote adsorption like glass
Minimally reactive
Chemically resistant to alcohol, acetone, and acrylates
Transparent, withstands EtO/gamma/steam sterilization
Temperature resistance, clarity and purity
Clarity, low birefringence, low moisture sensitivity
Low dielectric constant, thermoplastic
Not manufactured with BPA, phthalates, or halogens
Broad regulatory compliance
Related Grades for Injection Molding, Healthcare, Optics andDiagnostics
TOPAS 6013M-07 - broader processing window, best for blowmolding (IBM/ISBM)
TOPAS 6017S-04 - our most heat distortion resistant IM grade(HDT=170°C)
TOPAS IT X1 - impact grade for applications requiring extratoughness
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (260°C/2.16 kg) | 3.7 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） (260°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| 收缩率 1 | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 (饱和, 23°C) | 0 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 3000 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 60.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 2.5 | % | ISO 527-2/1A/50 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 (23°C) | 1.6 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 (23°C) | 15 | kJ/m² | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 (0.45 MPa, 未退火) | 150 | °C | ISO 75-2/B |
| 玻璃转化温度 | 158 | °C | ISO 11357-2 |
| 维卡软化温度 | 156 | °C | ISO 306/B50 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | > 1.0E+16 | ohms·cm | IEC 60093 |
| 相对电容率 | IEC 60250 | ||
| 1 kHz | 2.35 | IEC 60250 | |
| 10 kHz | 2.35 | IEC 60250 | |
| 耗散因数 (1.00 GHz) | 7.0E-5 | IEC 60250 | |
| 漏电起痕指数 | > 600 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 (1.60 mm) | HB | UL 94 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 折射率 | 1.530 | ISO 489 | |
| 透射率 | 91.0 | % | ISO 13468-2 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 130 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 料筒后部温度 | 240 到 270 | °C | |
| 料筒中部温度 | 250 到 310 | °C | |
| 料筒前部温度 | 260 到 310 | °C | |
| 射嘴温度 | 250 到 310 | °C | |
| 加工（熔体）温度 | 260 到 310 | °C | |
| 模具温度 | 110 到 145 | °C | |
| 注塑压力 | 50.0 到 110 | MPa | |
| 注射速度 | 中等偏快 | ||
| 保压 | 30.0 到 60.0 | MPa | |
| 背压 | < 15.2 | MPa | |
| 螺杆转速 | 50 到 200 | rpm |
| 注射说明 |
|---|
| Feed temperature:<110°C (<230°F)Max. residence time: |
| 备注 | |
|---|---|
| 1 . | Dependent on processing conditions and part design. |
长期供应：
工程塑胶原料：PC/ABS、PC、PPO、PPE、POM、PMMA、PA6、PA66、PA46、PA9T、PA6T、PA12、PA11、PBT、PET、ASA、AES、CA、SPS、PC/PBT、ASA/PC、PBT/PET、PC/PET、PA/ABS、PS/PA、PC/PS、POM/PTFE、PC/PTFE、PBT/PTFE/GF等。
通用塑胶原料：ABS、SAN（AS ）、GPPS、HIPS、PP、PE等。
特种工程塑胶原料：PPS、LCP、PEI、PEEK、PPA、PI、PSF、PES、PTFE、FEP、PVDF、PFA、PTT、PAA等。
改性工程塑料包括：加玻纤（GF）、碳纤（CF）、滑石粉、矿物、矿纤、钢纤、阻燃改性（UL94V-0、V-2、5VA）；增韧耐寒、抗紫外线（抗UV耐候）、抗静电、导电、电磁屏蔽、电磁干扰（EMI）、射频屏蔽等改性工程塑胶原料。热塑性弹性体：PVC、TPU、K胶、EVA、POE、TPR、TPE、SBS、SEBS、TPEE、TPV、TPO、TRS能够适合您各种硬度之需求及高透明、抗UV、高弹跳、多手感、高耐磨、抗变黄、阻燃、耐水解等高性能特征，能够与多种工程塑料，如PC、ABS、PA、PS、PP、PE等良好粘接。
主要经销产品涉及全球各dapinpai，如：美国杜邦（DUPONT）、奇美（Chimei）、美国液氮（LNP）、台湾南亚（NANYA）、 伊士曼（Eastman）、韩国三星（SAMSUNG）、美国普力万（POLYONE）、美国尔特普（RTP）、美国泰科纳（TICONA）、韩国锦湖（KUMHO）、德国巴斯夫（BASF）、德国拜耳（BAYER）、美国陶氏（DOW）、日本三菱（MITSUBISHI）、日本东丽（TORAY）、日本宇部（UBE）、日本宝理（POLY）、瑞士埃姆斯（EMS）、荷兰迪斯曼（DSM）、法国阿托（ATO）、日本出光（IDEMITSU）、日本帝人（TEIJIN）、沙伯基础（SABIC，原美国GE）等。