TOPAS®6013F-04
Cyclic Olefin Copolymer
Topas Advanced Polymers, Inc.
产品说明：
Product Description
TOPAS 6013F-04 is a high temperature, general purpose filmextrusion grade. It is a high clarity amorphous resin with highstiffness, moisture barrier, chemical resistance, thermoformabilityand purity for food and healthcare applications. It is used inmonolayer and blended cast applications, and in coextrusions andblends in both cast and blown processes, for a wide variety of filmand sheet products requiring excellent optics in applications suchas heat resistant blister, hot fill, and easy tear packaging. Ifperformance at elevated temperatures is not required, we also offerlower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
Pharmaceutical blisters
Decorative film and sheet
General packaging
Food packaging
Healthcare and food contact
Leading Attributes
Clarity, forming, barrier, heat resistance, halogen-free
Gloss, hardness, chemical resistance, forming
Easy or linear tear, heat resistance, hot fill
Not manufactured with BPA, phthalates, or halogens
Broad regulatory compliance
Related Grades for Packaging and Film Extrusion
TOPAS 5013F-04 - high temperature grade with higher flow
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） (230°C/2.16 kg) | 1.00 | cm³/10min | ISO 1133 |
| 吸水率 (饱和, 23°C) | 0 | % | ISO 62 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 70 | µm | |
| 拉伸模量 | ISO 527-3/1 | ||
| MD : 70 µm,铸造薄膜 | 2400 | MPa | ISO 527-3/1 |
| TD : 70 µm,铸造薄膜 | 2250 | MPa | ISO 527-3/1 |
| 拉伸应力 | ISO 527-3/50 | ||
| MD : 断裂, 70 µm,铸造薄膜 | 55.0 | MPa | ISO 527-3/50 |
| TD : 断裂, 70 µm,铸造薄膜 | 45.0 | MPa | ISO 527-3/50 |
| 伸长率 | ISO 527-3/50 | ||
| MD : 断裂, 70 µm,铸造薄膜 | 2.4 | % | ISO 527-3/50 |
| TD : 断裂, 70 µm,铸造薄膜 | 2.2 | % | ISO 527-3/50 |
| 落锤冲击 (70 µm, 铸造薄膜) | < 36 | g | ISO 7765-1 |
| 埃尔曼多夫抗撕强度 | ISO 6383-2 | ||
| MD : 70 µm,铸造薄膜 | 0.088 | N | ISO 6383-2 |
| TD : 70 µm,铸造薄膜 | 0.088 | N | ISO 6383-2 |
| 透氧率 (23°C, 70 µm, 挤塑薄膜, 50%RH) | 28 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| 水气透过率 (70 µm, 38°C, Cast Film, 90%RH) | 0.16 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 玻璃转化温度 | 138 | °C | ISO 11357-2 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (60°, 70.0 µm, 铸造薄膜) | > 100 | ISO 2813 | |
| 雾度 (70.0 µm, 铸造薄膜) | < 1.0 | % | ISO 14782 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 挤塑机进料部分 | 20 到 70 | °C | |
| 挤出机螺杆长径比L / D | > 28:1 | ||
| 料筒1区温度 | 230 到 240 | °C | |
| 料筒2区温度 | 250 到 260 | °C | |
| 料筒3区温度 | 250 到 260 | °C | |
| 料筒4区温度 | 250 到 260 | °C | |
| 口模温度 | 230 到 240 | °C |
| 挤压说明 |
|---|
| Head pressure: P > 140 bar / 2000 psi; Fine screen packs asneededScrew Speed: RPM > 50% nominalScrew design: Multi-purposeor barrier screw with mixing section Screw diameter > 60 mm /2.5 in Grooved Feed: Hot temperature: 120°C (212°F) |
TOPAS®具有与PMMA（聚甲基丙烯酸甲酯、丙烯酸树脂）相匹敌的光学性能以及具有高于PC（聚碳酸酯）的耐热性，还由于低吸水性而具有比PMMA和PC更加优良的尺寸稳定性等，在市场上获得了很高的评价。再有，TOPAS®还具有改善水蒸汽气密性，增加刚性、耐热性，能赋予易切割性等优点，作为适合于用作传统材料的改性用材料，它在包装材料领域里的开发活动正在推进之中。
COC 树脂TOPAS®是一种基于独创的茂金属催化剂技术的高品质和高纯度非晶性环状树脂。在标准要求很严的医疗器械装置和检查诊断器具等医疗领域，作为高品质和高成本的石英玻璃和PDMS（polydimethylsiloxane）等的替代材料，TOPAS® 具有zuijia特性和性价比。
以欧洲为中心的广大地区正在改用塑料来制作预充注射器以取代玻璃材料。预充注射器可改善制造过程中的破损废品率，减轻重量，不会产生金属类溶出物，同时还具有zuijia的水蒸气阻隔性（长期保存性）以及不亚于玻璃的高透明性等优良特性，因此是玻璃材料的zuijia替代材料。塑料瓶也保持着同样的特性，特别适合需要长期保存的场合。
TOPAS® 也被用于微量滴定板和生物芯片等检测器械。微量滴定板是用于生化分析和临床检查的一种实验和检测器械。用 TOPAS®制作的多孔型微量滴定板（384孔）有助于节省作业时间、减少样品用量并使数据更加精密，因而符合一次需要处理多种试样和信息的现代化学和生物学的流程。在对特殊有机溶剂（如DMSO = 二甲亚砜）和耐热性有要求的 DNA 和蛋白质分析等场合，TOPAS®堪称zuijia塑料材料。此外，由于荧光自发性低而耐药品（除油类和非极性溶剂）性高，因此也它适用于用 UV光等来进行检测的容器用途。
在以判定 BSE（疯牛病）和禽流感为目的的简易测量仪器中，有望被用作反应池（reactioncell）的生物芯片应具有细微转录性、低荧光自发性和耐热性等。TOPAS®既可满足上述特性要求，同时还具有其自身的高流动性所带来的高模具转录性以及良好的性价比，因而被认为是面向这一用途的zuijia塑料材料。
2包装材料编辑
作为一种多功能包装材料，COC塑胶原料 树脂TOPAS®以其水蒸气阻隔性、保香性、死褶性等优良特性而被广泛用于许多领域。
此外，它还具有良好的 PE（特别是 LLDPE）相溶性，可按任意比例与之混合，因而被用作 PE 改质剂。
富有创意的立袋（standing pouch）正在被日益广泛地用于洗涤剂和食品等领域。
为使立袋能够自立，其外装薄膜应具有一定强度（厚度）。
如果在密封层 PE 中掺入 TOPAS®，则可在保持薄膜整体刚性的同时实现外装薄膜的薄壁化并有效减少包装材料的用量。
TOPAS® 是一种水蒸气阻隔性好并且适用于 PTP 的材料。
它可提高热成型性，使角部厚度保持均匀，并可改善刚性，从而可以实现薄壁化。
此外，几乎所有的 TOPAS® 等级都在美国FDA药物管理文档（DMF #12132）和 FDA 设备管理文档（MAF#1043）中作了注册，因此在包装医疗品时尽可放心使用。
PET瓶的收缩标签以 PET 或 PS 为主，但也有一部分采用烯烃类树脂。
在烯烃中掺入 TOPAS® 可控制收缩特性（速度、收缩率），因此对异形瓶制作特别有效。
此外，烯烃类薄膜的优点还在于其优良的低温冲击性和弹性。
欧洲的部分国家从回收利用性（可通过比重差来区分瓶和薄膜）的观点出发采用了烯烃类薄膜。
热封性（hot tack）指标用来表示密封部分在刚刚密封后的熔融状态下的粘度。
此值偏低时，如果刚刚密封后就填充内容物，底部就会开裂。
通过掺入 TOPAS® 这一方法可提高热封性能，从而有效改善生产效能。
LLDPE 和 LDPE 的无延伸薄膜通常有粘性，并且用手难以开封。
通过掺入 TOPAS® 这一方法可控制撕裂强度（Elmendorf）并可使其具有易切割性和直进切割性。
已被用于食品包装和医疗包装等领域。